Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 饱和,23°C | ISO62 | 0.010 | % |
| Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 1.00 | cm3/10min |
| Melt Volume flow Rate | 230°C/2.16kg | ISO1133 | 6.00 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ISO527-2/1A/1000 | 2600 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Glass Transition Temperature | | ISO11357-2 | 65.0 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | MD | ISO527-3 | 1700 | Mpa |
| Tensile Modulus | TD | ISO527-3 | 2000 | Mpa |
| Tensile Stress | MD:断裂 | ISO527-3 | 55.0 | Mpa |
| Tensile Stress | TD:断裂 | ISO527-3 | 55.0 | Mpa |
| Tensile Elongation | MD:断裂 | ISO527-3 | 2.9 | % |
| Tensile Elongation | TD:断裂 | ISO527-3 | 3.6 | % |
| Elmendorf Tear Strength | MD | ISO6383-2 | 2.3 | N |
| Elmendorf Tear Strength | TD | ISO6383-2 | 2.4 | N |
| Gardner Impact | | ISO7765-1 | <36 | g |
| 38°C | ISO15106-3 | 0.800 | g·100µm/(m²·day |
| Oxygen Transmission Rate | 23°C,50%RH | ASTMD3985 | 17 | cm³·mm/m²/atm/24hr |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Gloss | 60° | ISO2813 | >100 | |
| Haze | | ISO14782 | <1.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.