| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | 横向流量 | ISO 2577 | 0.40 到 0.60 | % |
| Modeling Shrinkage | 流量 | ISO 2577 | 0.40 到 0.60 | % |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.40 | % |
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.10 | % |
| Melt Volume flow Rate | 240°C/5.0 kg | ISO 1133 | 20.0 | cm3/10min |
| Density | 23°C | ISO 1183 | 1.18 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | 屈服, 23°C | ISO 527-2/50 | 64.0 | Mpa |
| Tensile Strain | 屈服, 23°C | ISO 527-2/50 | 3.9 | % |
| Tensile Modulus | 23°C | ISO 527-2/1 | 2650 | Mpa |
| Nominal Tensile Strain at Break | 23°C | ISO 527-2/50 | 40 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45 MPa, 未退火 | ISO 75-2/B | 95.0 | °C |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火 | ISO 75-2/A | 85.0 | °C |
| Vicat Softening Temperature | | ISO 306/B120 | 103 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | IEC 60093 | 1.0E+16 | ohms |
| Volume Resistivity | 23°C | IEC 60093 | 1.0E+16 | ohms·cm |
| Relative Permittivity | 23°C, 100 Hz | IEC 60250 | 3.00 | |
| Relative Permittivity | 23°C, 1 MHz | IEC 60250 | 2.90 | |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|
| 240°C | ISO 11443-A | 150 | Pa·s |
| | | PC+ABS-FR(40) | |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Temperature () | | | 80 | °C |
| Dry Air Dryer | | | 4.0 | hr |
| Suggested Shot Size | | | 30 到 70 | % |
| Rear Temperature | | | 220 到 230 | °C |
| Middle Temperature | | | 225 到 235 | °C |
| Front Temperature | | | 230 到 240 | °C |
| Nozzle Temperature | | | 255 到 265 | °C |
| Back Pressure | | | 5.00 到 15.0 | Mpa |
| Vent Depth | | | 0.025 到 0.075 | mm |
| Suggested Max Moisture | | | < 0.020 | % |
| Processing (Melt) Temp | | | 240 到 270 | °C |
| Mold Temperature | | | 60 到 90 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | 23°C | ISO 180/A | 30 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Oxygen Index | | ISO 4589-2 | 34 | % |
| Flame Rating | 1.5 mm | UL 94 | V-0 | |
| Flame Rating | 2.0 mm | UL 94 | 5VB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.