Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 2781/JIS K7311 | 1.2 | |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | | ISO 868:2006(E) | 90±2/- | |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus (100%) | | ISO 37:2005(E) | 8.0 | Mpa |
| Flexural Modulus (300%) | | ISO 37 | 17 | Mpa |
| tensile strength | | ISO 37 | 43 | Mpa |
| Tensile Elongation | 断裂 | ISO 37 | 500 | % |
| Shore Hardness (Shore A) | | ASTM D2240/ISO 868 | 90+－2 | Shore A |
| 100% Secant | | ASTM D412/ISO 527 | 8 | Mpa/Psi |
| 300% Secant | | ASTM D412/ISO 527 | 17 | Mpa/Psi |
| Tensile Strength | | ASTM D412/ISO 527 | 43 | Mpa/Psi |
| Tearing Strength | | ASTM D624/ISO 34 | 130 | n/mm² |
| Tearing Strength | | ISP 34-1:2004(E) | 130 | kN/m |
| Flexural Strength | | ASTM D2630/ISO 4662 | 39 | % |
| Taber Abrasion Resistance | | DIN 53516 | 35 | mg |
| Flexural Strength | | ISO 4662 | 39 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Glass Transition Temperature | | ASTM D3417 | -35 | °C |
| Glass Transition Temperature | | ASTM D3418/ISO 815 | －35 | ℃（℉） |
| Vicat Softening Temperature | | ISO 306 | 115 | °C |
| Vicat Softening Temperature | | ASTM D1525/ISO R306 | 115 | ℃（℉） |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying conditions | | | 90℃ 2－3小时 | |
| Processing temperature | | | 155－175 | °C |
| Processing temperature | | | 185－195 | °C |
| Processing temperature | | | 185－190 | °C |
| Processing temperature | | | 190－200 | °C |
| Mold Temperature | | | 20－30 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.