| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD:23°C,2.00mm | ISO294-4 | 0.90 | % |
| Modeling Shrinkage | MD:23°C,2.00mm | ISO294-4 | 0.40 | % |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.90 | % |
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 1.9 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | 断裂,23°C | ISO527-2 | 195 | Mpa |
| Tensile Strain | 断裂,23°C | ISO527-2 | 3.0 | % |
| Flexural Stress | 23°C | ISO178 | 270 | Mpa |
| Tensile Modulus | 23°C | ISO527-2 | 10000 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 9600 | Mpa |
| Fish 'sratio' | 23°C | ISO527 | 0.40 | |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO75-2/B | 260 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/A | 250 | °C |
| RTIElec | 0.75mm | UL746 | 120 | °C |
| RTIElec | 1.5mm | UL746 | 120 | °C |
| RTIElec | 3.0mm | UL746 | 120 | °C |
| Evolution Calendar intelligent importer | 0.75mm | UL746 | 85.0 | °C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 85.0 | °C |
| Evolution Calendar intelligent importer | 3.0mm | UL746 | 105 | °C |
| RTIStr | 0.75mm | UL746 | 115 | °C |
| RTIStr | 1.5mm | UL746 | 120 | °C |
| RTIStr | 3.0mm | UL746 | 120 | °C |
| Linear thermal expansion coefficient | MD：23to55°C,2.00mm | ISO11359-2 | 2.2E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD：23to55°C,2.00mm | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| Melting temperature | | ISO11357-3 | 260 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Arc Resistance | 3.00mm | ASTMD495 | PLC5 | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC1 | |
| Dielectric Strength | 1.00mm | IEC60243 | 24 | KV/mm |
| Comparative Tracking Index | 3.00mm | IEC60112 | 600 | V |
| Volume Resistivity | 3.00mm | IEC60093 | 1E+14 | ohms·cm |
| High Amp Arc Ignition | 0.75mm | UL746 | PLC0 | |
| High Amp Arc Ignition | 1.5mm | UL746 | PLC0 | |
| High Amp Arc Ignition | 3.0mm | UL746 | PLC0 | |
| Hot-wire Ignition | 0.75mm | UL746 | PLC4 | |
| Hot-wire Ignition | 1.5mm | UL746 | PLC4 | |
| Hot-wire Ignition | 3.0mm | UL746 | PLC4 | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179 | 65 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 75 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 3.0mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.