Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | 横向流量 | 内部方法 | 1.3 | % |
| Modeling Shrinkage | 流量 | 内部方法 | 0.10 | % |
| Moisture Absorption | 饱和 | ASTM D570 | 0.020 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | | ASTM D638 | 150 | Mpa |
| Tensile Elongation | 断裂 | ASTM D638 | 5.0 | % |
| Flexural Modulus | 23°C | ASTM D790 | 12300 | Mpa |
| Flexural Modulus | 200°C | ASTM D790 | 6300 | Mpa |
| Flexural Strength | 23°C | ASTM D790 | 139 | Mpa |
| Flexural Strength | 200°C | ASTM D790 | 39.0 | Mpa |
| Shearing Strength | | ASTM D732 | 52.0 | Mpa |
| Poisson Ratio | | ASTM D785 | 0.49 | |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8 MPa, 未退火 | ASTM D648 | 313 | °C |
| Thermal Conductivity | | JIS R2618 | 0.57 | W/m/K |
| Linear thermal expansion coefficient | 流动 : 150°C | 内部方法 | 1.4E-5 | cm/cm/°C |
| Linear thermal expansion coefficient | 横向 : 150°C | 内部方法 | 6.2E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Comparative Tracking Index | | IEC 60112 | 145 | V |
| Dissipation Factor? | 1 kHz | ASTM D150 | 0.018 | |
| Dissipation Factor? | 1 MHz | ASTM D150 | 0.034 | |
| Dielectric Constant | 1 kHz | ASTM D150 | 4.50 | |
| Dielectric Constant | 1 MHz | ASTM D150 | 3.90 | |
| Arc Resistance | | ASTM D495 | 130 | sec |
| Volume Resistivity | | ASTM D257 | 1.0E+15 | ohms·cm |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Time | | | 4.0 到 24 | hr |
| Rear Temperature | | | 330 到 350 | °C |
| Middle Temperature | | | 350 到 370 | °C |
| Front Temperature | | | 370 到 390 | °C |
| Nozzle Temperature | | | 370 到 390 | °C |
| Back Pressure | | | 1.00 到 5.00 | Mpa |
| Screw Speed | | | 50 到 100 | rpm |
| Injection Pressure | | | 120 到 160 | Mpa |
| Injection Rate | | | 中等偏快 | |
| Drying Temperature | | | 130 | °C |
| Processing (Melt) Temp | | | 380 | °C |
| Mold Temperature | | | 40 到 160 | °C |
| Holding Pressure | | | 40.0 到 60.0 | Mpa |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Unnotched Izod Impact Strength | 6.40 mm | ASTM D256 | 520 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R 级 | ASTM D785 | 91 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| | 内部方法 | 330 | °C |
| Oxygen Index | | ISO 527-1,-2(JIS K7161,7162) | 48 | % |
| Flame Rating | 0.30 mm, NC, BK | UL 94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.