Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 饱和,23°C,2.00mm | ISO62 | 4.5 | % |
| Modeling Shrinkage | TD | ISO294-4 | 0.60 | % |
| Modeling Shrinkage | MD | ISO294-4 | 0.20 | % |
| SpecificHeatCapacityofMelt | | | 1860 | J/kg/°C |
| ThermalConductivityofMelt | | | 0.25 | W/m/K |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Creep Modulus | 1hr | ISO899-1 | -- | Mpa |
| Poisson Ratio | | ISO527 | 0.39 | |
| Tensile Creep Modulus | 1000hr | ISO899-1 | -- | Mpa |
| Flexural Stress | | ISO178 | 300 | Mpa |
| Tensile Stress | 断裂 | ISO527-2 | 210 | Mpa |
| Tensile Strain | 断裂 | ISO527-2 | 2.4 | % |
| Tensile Modulus | | ISO527-2 | 12000 | Mpa |
| Flexural Modulus | | ISO178 | 10300 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO75-2/B | 284 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/A | 260 | °C |
| Linear thermal expansion coefficient | MD：-- | ISO11359-2 | 1.8E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | MD：-40to23°C | ISO11359-2 | 1.8E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD：-- | ISO11359-2 | 5.5E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD：-40to23°C | ISO11359-2 | 5.5E-05 | cm/cm/°C |
| Melting Temperature | | ISO11357-3 | 300 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Relative Permittivity | 100Hz | IEC60250 | 4.00 | |
| Relative Permittivity | 1MHz | IEC60250 | 4.00 | |
| Comparative Tracking Index | | IEC60112 | 600 | V |
| Dielectric Strength | | IEC60243-1 | 36 | KV/mm |
| Surface Resistivity | | IEC60093 | -- | ohms |
| Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 60 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 70 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M计秤 | ISO2039-2 | 108 | |
| Rockwell Hardness | R计秤 | ISO2039-2 | 124 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.9mm | UL94 | HB | |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 0.9mm | IEC60695-11-10,-20 | HB | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
| Oxygen Index | | ISO4589-2 | 24 | % |
| FMVSS Flammability | | FMVSS302 | B | |
| Burning Rate | 1.00mm | ISO3795 | 23 | mm/min |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| Odor | | VDA270 | 4.00 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.