Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 7.0to9.0 | g/10min |
| Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 7.0to9.0 | g/10min |
| Methyl Acrylate Content | | | 18.0to22.0 | wt% |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation | 断裂,模压成型 | ASTMD638 | 800 | % |
| Flexural Modulus | 模压成型 | ASTMD790 | 20.0 | Mpa |
| Flexural Modulus | 模压成型 | ISO178 | 20.0 | Mpa |
| Tensile Strength | 断裂,模压成型 | ASTMD638 | 9.00 | Mpa |
| Tensile Stress | 断裂,模压成型 | ISO527-2 | 9.00 | Mpa |
| Tensile Strain | 断裂,模压成型 | ISO527-2 | 800 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melting temperature | | ISO11357-3 | 76.0 | °C |
| Vicat Softening Temperature | | ISO306/A | 46.0 | °C |
| Vicat Softening Temperature | | ASTMD15252 | 46.0 | °C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | 邵氏A,模压成型 | ASTMD2240 | 83 | |
| ShoreHardness | ShoreA,CompressionMolded | ISO868 | 83 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.