Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 饱和,23°C | ISO62 | 0.45 | % |
| Melt Viscosity | 400°C | ISO11443 | 350 | Pa·s |
| | 内部方法 | 11.0 | CM |
| Modeling Shrinkage | TD | ISO294-4 | 1.3 | % |
| Modeling Shrinkage | MD | ISO294-4 | 1.0 | % |
| Moisture Absorption | 100°C | ISO62 | 0.550 | |
| Density / Specific Gravity | | ISO1183 | 1.30 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Compressive Stress | 23°C | ISO604 | 125 | Mpa |
| Compressive Stress | 120°C | ISO604 | 70.0 | Mpa |
| Flexural Stress | 3.5%Strain,23°C | ISO178 | 125 | Mpa |
| Flexural Stress | 23°C6 | ISO178 | 165 | Mpa |
| Flexural Stress | 125°C | ISO178 | 85.0 | Mpa |
| Flexural Stress | 175°C | ISO178 | 19.0 | Mpa |
| Flexural Stress | 275°C | ISO178 | 12.5 | Mpa |
| Tensile Stress | 屈服,23°C | ISO527-2 | 98.0 | Mpa |
| Tensile Strain | 断裂,23°C | ISO527-2 | 45 | % |
| Tensile Modulus | 23°C | ISO527-2 | 4000 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 3800 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/Af | 152 | °C |
| Deflection Temperature Under Load? | 1.8MPa,退火 | ISO75-2/Af | 160 | °C |
| RTIElec | | UL746 | 260 | °C |
| Evolution Calendar intelligent importer | | UL746 | 180 | °C |
| RTIStr | | UL746 | 240 | °C |
| Linear thermal expansion coefficient | MD：<143°C | ISO11359-2 | 4.5E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | MD：>143°C | ISO11359-2 | 1.2E-04 | cm/cm/°C |
| Linear thermal expansion coefficient | TD：<143°C | ISO11359-2 | 5.5E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD：>143°C | ISO11359-2 | 1.4E-04 | cm/cm/°C |
| Melting temperature | | ISO11357-3 | 343 | °C |
| Glass Transition Temperature | --7 | ISO11357-2 | 143 | °C |
| Glass Transition Temperature | --8 | ISO11357-2 | 150 | °C |
| Thermal Conductivity | 23°C9 | ISO22007-4 | 0.29 | W/m/K |
| Thermal Conductivity | 23°C10 | ISO22007-4 | 0.32 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Comparative Tracking Index | | IEC60112 | 150 | V |
| Dielectric Strength | 2.00mm | IEC60243-1 | 23 | KV/mm |
| Dielectric Strength | 0.0500mm | IEC60243-1 | 200 | KV/mm |
| Dissipation Factor? | 23°C,1MHz | IEC60250 | 4E-03 | |
| Dielectric Constant | 23°C,50Hz | IEC60250 | 3.00 | |
| Dielectric Constant | 23°C,1kHz | IEC60250 | 3.10 | |
| Dielectric Constant | 200°C,50Hz | IEC60250 | 4.50 | |
| Volume Resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| Volume Resistivity | 125°C | IEC60093 | 1E+15 | ohms·cm |
| Volume Resistivity | 225°C | IEC60093 | 1E+09 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | NoBreak | |
| Notched Izod impact strength | 23°C | ISO180 | NoBreak | |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 7.0 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/A | 8.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | 邵氏D,23°C | ISO868 | 85 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Glow Wire Flammability Index | 2.0mm | IEC60695-2-12 | 960 | °C |
| Oxygen Index | --11 | ISO4589-2 | 24 | % |
| Oxygen Index | --12 | ISO4589-2 | 35 | % |
| Toxicity | COcontent | NES713 | 0.0740 | |
| Toxicity | CO2content | NES713 | 0.150 | |
| Toxicity | Totalgases | NES713 | 0.220 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.