Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | Flow,3.20mm | ASTM D-955 | 0.50-0.70 | % |
| Density | | ASTM D-792 | 1.17 | g/cm |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending yield strength | 50.0mm Span | ASTM D-790 | 73.1 | Mpa |
| Tensile Elongation?(Yield) | | ASTM D-638 | 2.1 | % |
| Tensile Strength(Break) | | ASTM D-638 | 35.2 | Mpa |
| IZOD Notch Impact Strength | 23℃ | ASTM D-256 | 267 | J/m |
| Tensile Modulus | | ASTM D-638 | 2410 | Mpa |
| Flexural Modulus | 50.0mm Span | ASTM D-790 | 2720 | Mpa |
| Tensile Strength(Yield) | | ASTM D-638 | 42.7 | Mpa |
| Tensile Elongation?(Break) | | ASTM D-638 | 11 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear thermal expansion coefficient | Flow,-40TO40℃ | ASTM E-831 | 0.000079 | cm/cm/℃ |
| Linear thermal expansion coefficient | Transverse,-40TO40℃ | ASTM E-831 | 0.000079 | cm/cm/℃ |
| Deflection Temperature Under Load? | 0.45MPa，未退火，3.20mm | ASTM D-648 | 83.9 | ℃ |
| Deflection Temperature Under Load? | 1.80MPa，未退火，3.20mm | ASTM D-648 | 72.2 | ℃ |
| Vicat Softening Temperature | | ASTM D-1525 | 90.0 | ℃ |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 230℃/3.8kg | ASTM D-1238 | 6.8 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.