ABS POLYLAC®  PA-756 TAIWAN CHIMEI

286
  • Properties:
    High gloss
    High mobility
    High rigidity
  • Usages:
    Home appliance components
    small home appliances
  • Certificates:
    UL
    MSDS
    RoHS

Technical Data Sheet

Physical PropertiesTest ConditionTest MethodTest ResultUnit
Melt Mass-Flow Rate200°C/5.0kgASTMD12384.4g/10min
Melt Volume flow Rate220°C/10.0kgISO113340.0cm3/10min
Density / Specific Gravity--3ASTMD7921.05g/cm³
Density / Specific Gravity23°CISO11831.05g/cm³
Modeling ShrinkageISO294-40.40到0.70%
Mechanical PropertiesTest ConditionTest MethodTest ResultUnit
Tensile Strength屈服4ASTMD63846.9Mpa
Tensile Strength屈服ISO527-2/5045.0Mpa
Tensile Strength断裂ISO527-2/5032.0Mpa
Tensile Elongation断裂4ASTMD63820%
Tensile Elongation断裂ISO527-2/5030%
Flexural Modulus--5ASTMD7902550Mpa
Flexural Modulus--6ISO1782100Mpa
Flexural Strength--5ASTMD79074.3Mpa
Flexural Strength--6ISO17872.0Mpa
Thermal PropertiesTest ConditionTest MethodTest ResultUnit
Deflection Temperature Under Load?1.8MPa,退火ISO75-2/A98.0°C
Deflection Temperature Under Load?1.8MPa,未退火ASTMD648,ISO75-2/A83.0°C
Deflection Temperature Under Load?1.8MPa,退火ASTMD64895.0°C
Vicat Softening Temperature--ASTMD15257105°C
Vicat Softening Temperature--ISO306/A50104°C
Vicat Softening Temperature--ISO306/B5096.0°C
Linear thermal expansion coefficientMDISO11359-28.9E-05cm/cm/°C
Impact PropertiesTest ConditionTest MethodTest ResultUnit
Charpy Notched Impact Strength-30°CISO1799.0kJ/m²
Charpy Notched Impact Strength23°CISO17917kJ/m²
Notched Izod Impact Strength23°C,3.20mmASTMD256170J/m
Notched Izod Impact Strength23°C,6.40mmASTMD256160J/m
Notched Izod Impact Strength-30°CISO180/1A8.0kJ/m²
Notched Izod Impact Strength23°CISO180/1A16kJ/m²
hardnessTest ConditionTest MethodTest ResultUnit
Rockwell HardnessR级ASTMD785115
FlammabilityTest ConditionTest MethodTest ResultUnit
UL flame retardant rating1.5mmUL94HB
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.