PA66 Zytel® 408HS DUPONT USA
192
- Properties:enhanceTougheningThermal stabilityHigh impact resistanceHigh temperature resistan
- Usages:Industrial machineryAutomotive sector
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1.09 | ||
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 1.2 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption (24hr) | ASTM D570 | 1.2 | % | |
| Moisture Absorption (Saturation) | ASTM D570 | 7.0 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength (Yield) | ASTM D638 | 62.7 | Mpa | |
| Rockwell hardness R | ASTM D-785 | 50%RH｜R102 | ||
| ASTM D-785 | DAM｜R115 | |||
| Rockwell Hardness(M-Scale) | ASTM D-785 | DAM｜M71 | ||
| ASTM D-785 | 50%RH｜M50 | |||
| Notched Izod Impact Strength | 23℃ | ASTM D-256 | DAM｜230 | J/m |
| 23℃ | ASTM D-256 | 50%RH｜240 | J/m | |
| Tensile Modulus | 23℃ | ASTM D-790 | DAM｜1965 | Mpa |
| 23℃ | ASTM D-790 | 50%RH｜1103 | Mpa | |
| Durometer Hardness | ASTM D-676 | DAM｜83 | ||
| ASTM D-676 | 50%RH｜76 | |||
| Tensile Elongation (Break) | ASTM D-638 | DAM｜5 | % | |
| ASTM D-638 | 50%RH｜15 | % | ||
| Tensile Strength (Yield) | 23℃ | DAM｜60.7 | Mpa | |
| 23℃ | 50%RH｜51.7 | Mpa | ||
| Tensile Elongation?(Break) | ASTM D638 | 50 | % | |
| 23℃ | ASTM D-638 | DAM｜80 | % | |
| 23℃ | ASTM D-638 | 50%RH｜270 | % | |
| ASTM D638/ISO 527 | 80 | % | ||
| Tensile Strength | ASTM D638/ISO 527 | 62.1 | kg/cm²(MPa)[Lb/in²] | |
| 23℃ | ASTM D-638 | 50%RH｜51.7 | Mpa | |
| 23℃ | ASTM D-638 | DAM｜62.1 | Mpa | |
| Tensile Elongation | ASTM D638/ISO 527 | 60.7 | % | |
| Flexural Modulus | ASTM D790 | 2070 | Mpa | |
| Tensile Impact Strength | 长试样23℃ | ASTM D-1822 | DAM｜550 | kJ/m² |
| 长试样23℃ | ASTM D-1822 | 50%RH｜1680 | kJ/m² | |
| 短试样23℃ | ASTM D-1822 | DAM｜189 | kJ/m² | |
| 短试样23℃ | ASTM D-1822 | 50%RH｜265 | kJ/m² | |
| Notched Impact Strength | ASTM D256 | 134 | J/m |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Brittleness Temperature | ASTM D-746 | DAM｜-104 | °C | |
| ASTM D-746 | 50%RH｜-84 | °C | ||
| Deflection Temperature Under Load? | 66 psi， 未退火 | ASTM D648 | 184 | °C |
| Melting Temperature | 255 | ℃（℉） | ||
| Fisher Johns法 | ASTM D-789 | DAM｜255 | °C | |
| Fisher Johns法 | ASTM D-789 | 50%RH｜255 | °C | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 7×10-5 | mm/mm.℃ | |
| Oxygen Index | ASTM D2863 | 23 | % | |
| Thermal distortion temperature | 18×106Pa | ASTM D-648 | DAM｜75 | °C |
| 18×106Pa | ASTM D-648 | 50%RH｜- | °C | |
| (0.5)×106Pa | ASTM D-648 | DAM｜230 | °C | |
| (0.5)×106Pa | ASTM D-648 | 50%RH｜- | °C | |
| Coefficient of Linear Thermal Expansion | 平行流动方向 | ASTM E831 | 0.00010 | cm/cm/ ℃ |
| ASTM D-696 | DAM｜7×10-5 | m/m/℃ | ||
| ASTM D-696 | 50%RH｜- | m/m/℃ | ||
| Flame Rating | UL 94 | DAM｜94 | ||
| UL 94 | 50%RH｜HB | |||
| Peak Crystallization Temperature | ASTM D-2177 | DAM｜270 | °C | |
| ASTM D-2177 | 50%RH｜- | °C | ||
| Heat Deflection Temperature | 13.8MPa，50℃ | ASTM D-621 | DAM｜1.4 | % |
| 13.8MPa，50℃ | ASTM D-621 | 50%RH｜- | % | |
| Flame Rating | UL 94 | HB |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Constant | ASTM D150/IEC 60250 | 3.1 | ||
| 103Hz(cps) | ASTM D-150 | DAM｜3.1 | ||
| 100Hz(cps) | ASTM D-150 | 50%RH｜4.8 | ||
| 106Hz(cps) | ASTM D-150 | DAM｜2.9 | ||
| 106Hz(cps) | ASTM D-150 | 50%RH｜3.3 | ||
| Volume Resistivity | ASTM D257/IEC 60093 | 10 | Ω.cm | |
| ASTM D-257 | DAM｜1013 | Ω.m | ||
| ASTM D-257 | 50%RH｜1013 | Ω.m | ||
| Dissipation Factor? | 100Hz(cps) | ASTM D-150 | DAM｜0.02 | |
| 100Hz(cps) | ASTM D-150 | 50%RH｜0.1 | ||
| 103Hz(cps) | ASTM D-150 | DAM｜0.02 | ||
| 103Hz(cps) | ASTM D-150 | 50%RH｜0.11 | ||
| 106Hz(cps) | ASTM D-150 | DAM｜0.02 | ||
| 106Hz(cps) | ASTM D-150 | 50%RH｜0.10 |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | 24小时浸渍(23℃) | ASTM D-570 | DAM｜1.2 | % |
| 24小时浸渍(23℃) | ASTM D-570 | 50%RH｜- | % | |
| 饱和(23℃) | ASTM D-570 | DAM｜7.0 | % | |
| 饱和(23℃) | ASTM D-570 | 50%RH｜- | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.