MABS TR557 INP LG CHEM KOREA

255

Properties:
Transparency level
High impact
Usages:
electronic product
Electronic appliances
Certificates:
UL
TDS
Compare

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	220°C/10.0 kg	ASTM D1238	21	g/10 min
Modeling Shrinkage - Flow	23°C, 3.20 mm, 注塑	ASTM D955	0.40 到 0.70	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Elongation	屈服, 23°C, 3.20 mm, 注塑	ASTM D638	> 5.0	%
Tensile Elongation	Tensile Elongation	断裂, 23°C, 3.20 mm, 注塑	ASTM D638	15	%
Tensile Modulus	23°C, 3.20 mm, 注塑	ASTM D638	2050	Mpa
Flexural Modulus	23°C, 3.20 mm, 注塑	ASTM D790	2250	Mpa
Flexural Strength	23°C, 3.20 mm, 注塑	ASTM D790	71.0	Mpa
Tensile Strength	屈服, 23°C, 3.20 mm, 注塑	ASTM D638	48.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature		ASTM D15257	89.0	°C
Deflection Temperature Under Load?	1.8 MPa, 未退火, 6.40 mm, 注塑	ASTM D648	81.0	°C
RTI		UL 746	50.0	°C
RTI Imp		UL 746	50.0	°C
RTI Elec		UL 746	50.0	°C

Injection	Test Result	Unit
Drying Temperature	80 到 90	°C
Processing (Melt) Temp	190 到 220	°C
Mold Temperature	40 到 60	°C
Drying Time	2.0 到 4.0	hr
Rear Temperature	180 到 200	°C
Middle Temperature	190 到 210	°C
Front Temperature	200 到 220	°C
Nozzle Temperature	190 到 220	°C
Back Pressure	29.4 到 58.8	Mpa
Screw Speed	30 到 60	rpm

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R 级, 23°C, 注塑	ASTM D785	107

optical performance	Test Condition	Test Method	Test Result	Unit
Haze	注塑	ASTM D1003	2.0	%
Transmittance	3200 µm, 注塑	ASTM D1003	90.0	%

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.5 mm	UL 94	HB
Flame Rating	Flame Rating	3.0 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.