Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | 横向流量 | ISO 294-4 | 0.80 | % |
| Modeling Shrinkage | 流量 | ISO 294-4 | 0.30 | % |
| Moisture Absorption | 饱和, 23°C, 2.00 mm | ISO 62 | 4.2 | % |
| Moisture Absorption | 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.2 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | 断裂 | ISO 527-2 | 250 | Mpa |
| Tensile Strain | 断裂 | ISO 527-2 | 2.3 | % |
| Tensile Creep Modulus | 1 hr | ISO 899-1 | -- | Mpa |
| Tensile Creep Modulus | 1000 hr | ISO 899-1 | -- | Mpa |
| Tensile Modulus | | ISO 527-2 | 17000 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45 MPa, 未退火 | ISO 75-2/B | 262 | °C |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火 | ISO 75-2/A | 260 | °C |
| Linear thermal expansion coefficient | 流动 | ISO 11359-2 | 1.5E-5 | cm/cm/°C |
| Linear thermal expansion coefficient | 横向 | ISO 11359-2 | 7.5E-5 | cm/cm/°C |
| Thermal Conductivity | | | 0.46 | W/m/K |
| Glass Transition Temperature | | ISO 11357-2 | 80.0 | °C |
| Melting Temperature | | ISO 11357-3 | 262 | °C |
| Vicat Softening Temperature | | ISO 306/B50 | 255 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | IEC 62631-3-2 | -- | ohms |
| Volume Resistivity | | IEC 62631-3-1 | 1.0E+13 | ohms·m |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Density | | | 1.40 | g/cm³ |
| Ejection Temperature | | | 210 | °C |
| | | 1870 | J/kg/°C |
| | | 0.31 | W/m/K |
| Odor | | VDA 270 | 3.00 | |
| | VDA 277 | 6.50 | µgC/g |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Temperature | | | 80 | °C |
| Drying time - Hot air dryer | | | 2.0 到 4.0 | hr |
| Suggested Max Moisture | | | 0.20 | % |
| Processing (Melt) Temp | | | 285 到 305 | °C |
| | | 295 | °C |
| Mold Temperature | | | 50 到 90 | °C |
| | | 100 | °C |
| Holding Pressure | | | 50.0 到 100 | Mpa |
| Holding Pressure | Drying Recommended | | yes | |
| | | 3.00 | s/mm |
| | | 12 | m/min |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 90 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 100 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 0.8 mm | UL 94, IEC 60695-11-10, -20 | HB | |
| Flame Rating | 1.5 mm | UL 94, IEC 60695-11-10, -20 | HB | |
| FMVSS Flammability | | FMVSS 302 | SE | |
| Haze | | ISO 6452 | 4.0E-4 | g |
| Oxygen Index | | ISO 4589-2 | 24 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.