Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 1.8 | g/10min |
| Vinyl Acetate Content | | | 18.0 | wt% |
| Density / Specific Gravity | | ASTMD1505 | 0.938 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation | 断裂 | ASTMD638 | 800 | % |
| Flexural Modulus | | ASTMD790 | 39.2 | Mpa |
| Tensile Strength | 屈服 | ASTMD638 | 4.41 | Mpa |
| Tensile Strength | 断裂 | ASTMD638 | 14.7 | Mpa |
| Coefficient of Friction | 吹塑薄膜 | ASTMD1894 | 0.50 | |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ASTMD1525 | 60.0 | °C |
| Brittleness Temperature | | ASTMD746 | -70.0 | °C |
| Melting temperature | | | 84.0 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Film Thickness - Tested) | | | 30 | µm |
| Secant Modulus | 1%正割,MD:30µm,吹塑薄膜 | ASTMD882 | 34.3 | Mpa |
| Secant Modulus | 1%正割,TD:30µm,吹塑薄膜 | ASTMD882 | 37.3 | Mpa |
| Tensile Elongation | MD:断裂,30µm,吹塑薄膜 | ASTMD882 | 500 | % |
| Tensile Elongation | TD:断裂,30µm,吹塑薄膜 | ASTMD882 | 600 | % |
| Elmendorf Tear Strength | MD:30µm,吹塑薄膜 | ASTMD1922 | 12 | g |
| Elmendorf Tear Strength | TD:30µm,吹塑薄膜 | ASTMD1922 | 29 | g |
| Tensile Strength | MD:屈服,30µm,吹塑薄膜 | ASTMD882 | 3.92 | Mpa |
| Tensile Strength | TD:屈服,30µm,吹塑薄膜 | ASTMD882 | 2.94 | Mpa |
| Tensile Strength | MD:断裂,30µm,吹塑薄膜 | ASTMD882 | 27.5 | Mpa |
| Tensile Strength | TD:断裂,30µm,吹塑薄膜 | ASTMD882 | 24.5 | Mpa |
| Gardner Impact | 30µm,吹塑薄膜 | ASTMD1709 | 650 | g |
| Film Thickness | | | 1.2-5.9mil(30-150µ | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | 邵氏A | ASTMD2240 | 8838 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Gloss | 45°,30.0µm,吹塑薄膜 | ASTMD2457 | 90 | |
| Haze | 30.0µm,吹塑薄膜 | ASTMD1003 | 3.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.