Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50到0.70 | % |
| Moisture Absorption | 24hr | ASTMD570 | 0.15 | % |
| Moisture Absorption | 平衡,23°C | ASTMD570 | 0.35 | % |
| Moisture Absorption | 平衡,100°C | ASTMD570 | 0.58 | % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 15 | g/10min |
| Specific Volume | | ASTMD792 | 0.835 | cm³/g |
| Outdoor Suitability | | UL746C | f1 | |
| Density / Specific Gravity | -- | ASTMD792 | 1.21 | g/cm³ |
| Density / Specific Gravity | -- | ASTMD792 | 1.22 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | 屈服 | ASTMD638 | 62.1 | Mpa |
| Tensile Strength | 断裂 | ASTMD638 | 55.8 | Mpa |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17转轮 | ASTMD1044 | 10.0 | mg |
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2240 | Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 7.0 | % |
| Tensile Elongation | 断裂 | ASTMD638 | 90 | % |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 91.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ASTMD15256 | 152 | °C |
| RTI | | UL746 | 130 | °C |
| Thermal Conductivity | | ASTMC177 | 0.19 | W/m/K |
| Linear thermal expansion coefficient | MD：-40到95°C | ASTME831 | 6.8E-05 | cm/cm/°C |
| Deflection Temperature Under Load? | 0.45MPa,未退火,6.40mm | ASTMD648 | 138 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火,6.40mm | ASTMD648 | 132 | °C |
| RTIElec | | UL746 | 130 | °C |
| Evolution Calendar intelligent importer | | UL746 | 120 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation Factor? | 50Hz | ASTMD150 | 9E-04 | |
| Dissipation Factor? | 60Hz | ASTMD150 | 9E-04 | |
| Dissipation Factor? | 1MHz | ASTMD150 | 0.010 | |
| Dielectric Constant | 50Hz | ASTMD150 | 3.01 | |
| Dielectric Constant | 60Hz | ASTMD150 | 3.01 | |
| Dielectric Constant | 1MHz | ASTMD150 | 2.96 | |
| Volume Resistivity | | ASTMD257 | >1.0E+17 | ohms·cm |
| Dielectric Strength | 3.20mm,inAir | ASTMD149 | 17 | KV/mm |
| Arc Resistance | | ASTMD495 | PLC7 | |
| Comparative Tracking Index | CTI | UL746 | PLC3 | |
| Hot-wire Ignition | HWI | UL746 | PLC1 | |
| High Amp Arc Ignition | HAI | UL746 | PLC2 | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC3 | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Gardner Impact | 23°C | ASTMD3029 | 169 | J |
| Unnotched Izod Impact Strength | 23°C | ASTMD4812 | 3200 | J/m |
| Tensile Impact Strength | | ASTMD1822 | 525 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ASTMD256 | 640 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R级 | ASTMD785 | 118 | |
| Rockwell Hardness | M级 | ASTMD785 | 70 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Oxygen Index | | ASTMD2863 | 35 | % |
| UL flame retardant rating | 1.47mm | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.