PBT VALOX™ 357X BK SABIC INNOVATIVE US
224
- Properties:Flame retardantUV resistance
- Usages:Electrical appliancesElectronic displayHousehold goodsLighting fixtures
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 250°C/5.0kg | ASTMD1238 | 9.6 | g/10min |
| 265°C/5.0kg | ASTMD1238 | 13 | g/10min | |
| 266°C/5.0kg | ASTMD1238 | 13 | g/10min | |
| Modeling Shrinkage | MD1 | 内部方法 | 1.1到1.8 | % |
| MD:3.20mm | 内部方法 | 1.0到1.4 | % | |
| TD2 | 内部方法 | 0.90到1.8 | % | |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.50 | % |
| 平衡,23°C,50%RH | ISO62 | 0.15 | % | |
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 8.00 | cm3/10min |
| 265°C/5.0kg | ISO1133 | 10.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 33.0 | mg |
| yield | ISO527-2/50 | 5.0 | % | |
| ISO527-2/50 | 50.0 | Mpa | ||
| fracture | ISO527-2/50 | 40.0 | Mpa | |
| ISO527-2/50 | 30 | % | ||
| Yield | ASTMD638 | 50.0 | Mpa | |
| Break | ASTMD638 | 40.0 | Mpa | |
| Yield | ASTMD638 | 5.0 | % | |
| Break | ASTMD638 | 30 | % | |
| 50.0mm Span | ASTMD790 | 2100 | Mpa | |
| ISO178 | 2000 | Mpa | ||
| ISO178 | 80.0 | Mpa | ||
| Yield,50.0mm Span | ASTMD790 | 78.0 | Mpa | |
| ASTMD638 | 2000 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 85.0 | °C | |
| 0.45MPa, Unannealed,3.20mm | ASTMD648 | 130 | °C | |
| ASTMD1525,ISO306/B501322 | 145 | °C | ||
| ASTMD1525,ISO306/A501423 | 180 | °C | ||
| ISO306/B120 | 150 | °C | ||
| Flow:-40 to 40°C | ASTME831 | 9.2E-05 | cm/cm/°C | |
| Flow:23 to 80°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| Flow:-40 to 40°C | ASTME831 | 8.4E-05 | cm/cm/°C | |
| Flow:23 to 80°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| 0.45MPa, Unannealed,100mm Span | ISO75-2/Be | 135 | °C | |
| 0.45MPa, Unannealed,3.20mm Span | ISO75-2/Bf | 130 | °C | |
| 1.8MPa, Unannealed,100mm Span | ISO75-2/Ae | 85.0 | °C | |
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 85.0 | °C | |
| Thermal Conductivity | ISO8302 | 0.17 | W/m/K | |
| RTI | UL746 | 140 | °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass | |
| RTIElec | UL746 | 120 | °C | |
| Evolution Calendar intelligent importer | UL746 | 120 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Comparative Tracking Index | CTI | UL746 | PLC3 | |
| Surface Resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume Resistivity | ASTMD257,IEC60093 | >1.0E+15 | ohms·cm | |
| Comparative Tracking Index | -- | IEC60112 | 225 | V |
| 解决方案B | IEC60112 | 100 | V | |
| ASTMD150 | 0.013 | |||
| IEC60250 | 1.3E-03 | |||
| ASTMD150,IEC60250 | 3.00 | |||
| Hot-wire Ignition | HWI | UL746 | PLC3 | |
| IEC60250 | 3.00 | |||
| IEC60250 | 2E-03 | |||
| IEC60250 | 2E-03 | |||
| IEC60250 | 3.00 | |||
| Arc Resistance | ASTMD495 | PLC6 | ||
| ASTMD149 | 25 | KV/mm | ||
| ASTMD149 | 17 | KV/mm | ||
| 0.800mm, in oil | IEC60243-1 | 34 | KV/mm | |
| 1.60mm,in Oil | IEC60243-1 | 25 | KV/mm | |
| 3.20mm,in Oil | IEC60243-1 | 17 | KV/mm | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC3 | |
| High Amp Arc Ignition | HAI | UL746 | PLC0 |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Viscosity | 260°C,1500sec^-1 | ISO11443 | 310 | Pa·s |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unnotched Izod Impact Strength | -30°C | ASTMD4812,ISO180/1U | 无断裂 | |
| 23°C | ASTMD4812,ISO180/1U | 无断裂 | ||
| ISO179/2C | 40 | kJ/m² | ||
| ASTMD256 | 500 | J/m | ||
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 35.0 | J |
| ISO179/1eA,ISO179/2C | 20 | kJ/m² | ||
| ISO179/1eA | 45 | kJ/m² | ||
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU,ISO179/2U | 无断裂 | |
| 23°C | ISO179/1eU,ISO179/2U | 无断裂 | ||
| ASTMD256 | 150 | J/m | ||
| ASTMD256 | 190 | J/m | ||
| ISO180/1A | 10 | kJ/m² | ||
| ISO180/1A | 20 | kJ/m² | ||
| ISO180/1A | 40 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R计秤 | ISO2039-2 | 115 | |
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 115 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen Index | ISO4589-2 | 30 | % | |
| UL flame retardant rating | 0.750mm | UL94 | V-0 | |
| 2.50mm | UL94 | 5VA | ||
| Glow Wire Flammability Index | 1.00mm | IEC60695-2-12 | 960 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.