Technical Data Sheet
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | | 12000 | Mpa |
| Charpy Notched Impact Strength | 23℃ | | 4 | KJ/m |
| Tensile Strength(Break) | | | 110 | Mpa |
| | | 2 | % |
| Tensile elongation modulus | 1h | | 9500 | Mpa |
| Tensile elongation modulus | 1000h | | 7500 | Mpa |
| Charpy impact strength | 23℃ | | 17 | KJ/m |
| Charpy impact strength | -30℃ | | 17 | KJ/m |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.80MPa | | 105 | °C |
| Deflection Temperature Under Load? | 0.45MPa | | 108 | °C |
| Vicat Softening Temperature | 50℃/H50n | | 109 | °C |
| Linear expansion coefficient | 平行方向 | | 0.25 | E-4/℃ |
| Flammability | 1.6mm | UL 94 | HB | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| 100Hz | | 70 | E-4 |
| 1MHz | | 100 | E-4 |
| Relative Arc Track Mathematical CTI | | | 600 | |
| Surface Resistivity | | | >1E15 | Ω |
| Dielectric Constant | 100Hz | | 3.5 | |
| Dielectric Constant | 1MHz | | 3.2 | |
| Volume Resistivity | | | >1E13 | Ω.m |
| Dielectric Strength | | | 39 | KV/mm |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|
| Oxygen Index | | | 20 | % |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | | | 0.25 | % |
| Density / Specific Gravity | | | 1360 | kg/m |
| Melt index | 220℃/10kg | | 5 | CM |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.