Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 24hr | ASTMD570 | 0.10 | % |
| Melt Mass-Flow Rate | 400°C/2.16kg | ASTMD1238 | 0.70 | g/10min |
| Modeling Shrinkage | MD:3.18mm | ASTMD955 | 0.20到0.40 | % |
| Modeling Shrinkage | TD:3.18mm | ASTMD955 | 1.4到1.6 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Compressive Strength | | ASTMD695 | 169 | Mpa |
| Shearing Strength | | ASTMD732 | 93.1 | Mpa |
| Poisson Ratio | | 7.58 | 0.34 | |
| Nominal Tensile Strain at Break | -- | ISO527-2/1A/5 | 2.7 | % |
| Nominal Tensile Strain at Break | --6 | ASTMD638 | 2.7 | % |
| Tensile Strength | 屈服5 | ASTMD638 | 158 | Mpa |
| Tensile Strength | 屈服 | ISO527-2/1A/5 | 165 | Mpa |
| Tensile Strength | -- | ASTMD638 | 158 | Mpa |
| Tensile Modulus | --5 | ASTMD638 | 10500 | Mpa |
| Tensile Modulus | -- | ISO527-2/1A/1 | 11400 | Mpa |
| Flexural Modulus | -- | ASTMD790 | 10300 | Mpa |
| Flexural Modulus | -- | ISO178 | 10700 | Mpa |
| Flexural Strength | -- | ASTMD790 | 271 | Mpa |
| Flexural Strength | -- | ISO178 | 246 | Mpa |
| Flexural Strength | 屈服 | ASTMD790 | 261 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,退火 | ASTMD648 | 315 | °C |
| Specific Heat | 50°C | DSC | 1300 | J/kg/°C |
| Specific Heat | 200°C | DSC | 1730 | J/kg/°C |
| Thermal Conductivity | | ASTME1530 | 0.29 | W/m/K |
| Glass Transition Temperature | | ASTMD3418 | 150 | °C |
| Linear thermal expansion coefficient | MD：-50到50°C | ASTME831 | 1.7E-05 | cm/cm/°C |
| Peak Melting Temperature | | ASTMD3418 | 340 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | 3.00mm | ASTMD149 | 17 | KV/mm |
| Surface Resistivity | | ASTMD257 | >1.9E+17 | ohms |
| Dielectric Constant | 60Hz | ASTMD150 | 3.44 | |
| Dielectric Constant | 1kHz | ASTMD150 | 3.44 | |
| Dielectric Constant | 1MHz | ASTMD150 | 3.41 | |
| Volume Resistivity | | ASTMD257 | 1.9E+17 | ohms·cm |
| Dissipation Factor? | 60Hz | ASTMD150 | 1E-03 | |
| Dissipation Factor? | 1kHz | ASTMD150 | 1E-03 | |
| Dissipation Factor? | 1MHz | ASTMD150 | 3E-03 | |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Viscosity | 400°C,1000sec^-1 | ASTMD3835 | 850 | Pa·s |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Unnotched Izod Impact Strength | -- | ISO180 | 56 | kJ/m² |
| Unnotched Izod Impact Strength | -- | ASTMD4812 | 960 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M级 | ASTMD785 | 100 | |
| Shore Hardness | 邵氏D,1秒 | ASTMD2240 | 91 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.6mm | UL94 | V-0 | |
| UL flame retardant rating | 20.3mm | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.