TPE Hytrel® 6356 DUPONT USA

219

Properties:
Thermal stability
Usages:
Electrical tools
Wire and cable
Industrial applications
pipeline
sheet
Automotive sector
Certificates:
UL
Compare
View Prices

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	ISO294-4	1.5	%
Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	1.5	%
Moisture Absorption	23°C,24hr	ISO62	0.50	%
	Moisture Absorption	饱和,23°C,2.00mm	ISO62	0.60	%
	Moisture Absorption	Moisture Absorption	平衡,23°C,2.00mm,50%RH	ISO62	0.20	%
Melt Mass-Flow Rate	230°C/2.16kg	ISO1133	9.0	g/10min
MediumDensity			1.06	g/cm³
SpecificHeatCapacityofMelt			2150	J/kg/°C
ThermalConductivityofMelt			0.15	W/m/K
Melt Volume flow Rate	230°C/2.16kg	ISO1133	8.50	cm3/10min
Density / Specific Gravity		ISO1183	1.22	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Nominal Tensile Strain at Break		ISO527-2	500	%
Abrasion Resistance		ISO4649	110	mm³
Tensile Creep Modulus	1000hr	ISO899-1	182	Mpa
Tensile Creep Modulus	Tensile Creep Modulus	1hr	ISO899-1	248	Mpa
Tensile Stress	屈服	ISO527-2	20.0	Mpa
	Tensile Stress	断裂	ISO527-2	43.0	Mpa
		Tensile Stress	5.0%应变	ISO527-2	12.0	Mpa
			Tensile Stress	10%应变	ISO527-2	15.0	Mpa
				Tensile Stress	50%应变	ISO527-2	18.8	Mpa
				Tensile Stress	Tensile Stress	100%应变	ISO527-2	19.0	Mpa
Tensile Strain	屈服	ISO527-2	31	%
Tensile Strain	Tensile Strain	断裂	ISO527-2	>300	%
Tensile Modulus		ISO527-2	280	Mpa
Flexural Modulus		ISO178	290	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,未退火	ISO75-2/B	80.0	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,未退火	ISO75-2/A	45.0	°C
Brittleness Temperature		ISO974	-96.0	°C
Vicat Softening Temperature	--	ISO306/A50	195	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B50	100	°C
Melting Temperature		ISO11357-3	210	°C
Linear thermal expansion coefficient	MD：--	ISO11359-2	1.9E-04	cm/cm/°C
	Linear thermal expansion coefficient	MD：-40to23°C	ISO11359-2	1.6E-04	cm/cm/°C
		Linear thermal expansion coefficient	TD：23to55°C	ASTME831	1.7E-04	cm/cm/°C
			Linear thermal expansion coefficient	TD：--	ISO11359-2	1.8E-04	cm/cm/°C
				Linear thermal expansion coefficient	TD：-40to23°C	ISO11359-2	1.5E-04	cm/cm/°C
				Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：EffectiveThermalDiffusivity	ISO11359-2	5.44E-08	m²/s
Glass Transition Temperature		ISO11357-2	0.00	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative Permittivity	100Hz	IEC60250	4.60
Relative Permittivity	Relative Permittivity	1MHz	IEC60250	4.10
Dielectric Strength		IEC60243-1	20	KV/mm
Surface Resistivity		IEC60093	>1.0E+15	ohms
Volume Resistivity		IEC60093	8E+13	ohms·cm
Dissipation Factor?	100Hz	IEC60250	0.012
Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	0.036

Elastomers Properties	Test Condition	Test Method	Test Result	Unit
Tearing Strength	横向流量	ISO34-1	150	kN/m
Tearing Strength	Tearing Strength	流量	ISO34-1	160	kN/m

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-40°C	ISO179/1eA	15	kJ/m²
	Charpy Notched Impact Strength	-30°C	ISO179/1eA	25	kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C,局部断裂	ISO179/1eA	120	kJ/m²
Notched Izod Impact Strength	-40°C	ISO180/1A	19	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	81	kJ/m²
Tensile Impact Strength	23°C	ISO8256/1	300	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Shore Hardness	邵氏D	ISO868	63
Shore Hardness	Shore Hardness	邵氏D,15秒	ISO868	57

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	HB
	UL flame retardant rating	3.0mm	UL94	HB
		UL flame retardant rating	1.5mm	IEC60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	3.0mm	IEC60695-11-10,-20	HB
Oxygen Index		ISO4589-2	21	%
FMVSS Flammability		FMVSS302	SE
Fogging-G-value	condensate	ISO6452	1E-04	g

Supplementary information	Test Condition	Test Method	Test Result	Unit
EmissionofOrganicCompounds		VDA277	2.50	µgC/g
Odor		VDA270	2.50

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

TPE Hytrel® 6356 DUPONT USA

Technical Data Sheet