Technical Data Sheet
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation | 断裂 | ASTM D-638 | ＞250 | % |
| Tensile Elongation | 断裂 | ASTM D-638 | ＞250 | % |
| Rockwell Hardness | 23℃ | ASTM D-785 | 100 | R scale |
| Flexural Modulus | | ASTM D-790 | 17000 | kg/cm2 |
| Tensile Strength | 50mm/min | ASTM D-638 | 380 | kg/cm2 |
| Tensile Strength | 50mm/min | ASTM D-638 | 380 | kg/cm2 |
| Tensile Strength (Break) | 50mm/min | ASTM D-638 | 200 | kg/cm2 |
| Izod Impact Strength | 1/4"，23℃ | ASTM D-256 | 3 | kg.cm/cm |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | 1kg | ASTM D-1525 | 155 | ℃ |
| Deflection Temperature Under Load? | 18.6kg/cm2(1/8") | ASTM D-648 | 65 | ℃ |
| Deflection Temperature Under Load? | 4.6kg/cm2(1/8") | ASTM D-648 | 110 | ℃ |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 230℃，2.16kg | ASTM D-1238 | 22 | g/10min |
| Melt index | 230℃，2.16kg | ASTM D-1238 | 22 | g/10min |
| Density | | ASTM D-1505 | 0.91 | g/cm³ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.