Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD：3.20mm | ASTMD955 | 0.29to0.36 | % |
| Modeling Shrinkage | TD：3.20mm | ASTMD955 | 0.31to0.38 | % |
| Modeling Shrinkage | TD:3.20mm | ISO2577 | 0.31to0.38 | % |
| Modeling Shrinkage | MD:3.20mm | ISO2577 | 0.29to0.36 | % |
| Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 13 | g/10min |
| Melt Mass-Flow Rate | 220°C/10.0kg | ISO1133 | 13 | g/10min |
| Density / Specific Gravity | | ASTMD792 | 1.10 | g/cm³ |
| Density / Specific Gravity | | ISO1183 | 1.10 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ASTMD638 | 2500 | Mpa |
| Flexural Modulus | | ISO178 | 2700 | Mpa |
| Flexural Modulus | | ASTMD790 | 2600 | Mpa |
| Tensile Strength | 断裂 | ASTMD638 | 34.0 | Mpa |
| Tensile Strength | 屈服 | ASTMD638 | 51.0 | Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 25 | % |
| Flexural Strength | | ASTMD790 | 74.0 | Mpa |
| Flexural Stress | | ISO178 | 85.0 | Mpa |
| Tensile Stress | 屈服 | ISO527-2/50 | 55.0 | Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 40.0 | Mpa |
| Tensile Strain | 断裂 | ISO527-2/50 | 20 | % |
| Tensile Modulus | | ISO527-2/50 | 2600 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,未退火,6.40mm | ASTMD648 | 98.0 | °C |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,4.00mm | ISO75-2/B | 91.0 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火,6.40mm | ASTMD648 | 92.0 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 78.0 | °C |
| Vicat Softening Temperature | | ISO306/B50 | 100 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | 23°C | ISO180/1A | 9.0 | kJ/m² |
| 23°C | ISO179/1eA | 8.0 | kJ/m² |
| Notched Izod Impact Strength | 23°C,3.18mm | ASTMD256 | 110 | J/m |
| Notched Izod Impact Strength | 23°C,6.35mm | ASTMD256 | 98 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R级 | ASTMD785 | 116 | |
| Rockwell Hardness | R级 | ISO2039-2 | 116 | |
| Pencil Hardness | | JISK5401 | H | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 3.0mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.