Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 190°C/2.16 kg | ISO 1133 | 0.40 | g/10 min |
| n-Butyl Acrylate Content | | 内部方法 | 17.0 | wt% |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melting temperature | | 内部方法 | 96.0 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | MD : 断裂, 100 µm, 吹塑薄膜 | ISO 527-3 | 29.0 | Mpa |
| Tensile Stress | TD : 断裂, 100 µm, 吹塑薄膜 | ISO 527-3 | 30.0 | Mpa |
| Tensile Elongation | MD : 断裂, 100 µm, 吹塑薄膜 | ISO 527-3 | 750 | % |
| Tensile Elongation | TD : 断裂, 100 µm, 吹塑薄膜 | ISO 527-3 | 850 | % |
| Elmendorf Tear Strength | MD : 100 µm, 吹塑薄膜 | ISO 6383-2 | 3.6 | N |
| Elmendorf Tear Strength | TD : 100 µm, 吹塑薄膜 | ISO 6383-2 | 3.9 | N |
| Gardner Impact | 100 µm, 吹塑薄膜 | ISO 7765-1 | > 1400 | g |
| Film Thickness (Tested) | | | 100 | µm |
| Extrusion | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Temperature | | | 180 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.