EAA PRIMACOR™ 1410 STYRON US
465
- Properties:High toughnessHeat sealing performancehigh strength
- Usages:film
Compare
View PricesTechnical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238,ISO1133 | 1.5 | g/10min |
| monomer Content | 内部方法 | 9.7 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Film Thickness (Tested) | um | 50.8 | ||
| Gardner Impact | 50.8um | g | ASTM D-1709B | 580 |
| 50.8um | g | ISO 7765-1/B | 580 | |
| Tensile Strength (Yield TD) | 50.8um | MPa | ASTM D-882 | 10.9 |
| 50.8um | MPa | ISO 527-3 | 10.9 | |
| Tensile Strength (Yield MD) | 50.8um | MPa | ISO 527-3 | 11.8 |
| 50.8um | MPa | ASTM D-882 | 11.8 | |
| Tensile Elongation | 断裂,模压成型4 | ASTMD638 | 640 | % |
| 断裂,模压成型 | ISO527-2/508 | 640 | % | |
| Tensile Strength | 屈服,模压成型4 | ASTMD638 | 8.39 | Mpa |
| 屈服,模压成型 | ISO527-2/508 | 8.39 | Mpa | |
| 断裂,模压成型4 | ASTMD638 | 22.5 | Mpa | |
| 断裂,模压成型 | ISO527-2/508 | 22.5 | Mpa | |
| Tensile Strength(Yield) | Compression Molded | MPa | ASTM D-638 | 8.39 |
| Compression Molded | MPa | ISO 527-2/508 | 8.39 | |
| Tensile Elongation?(Break) | Compression Molded | % | ASTM D-638 | |
| Compression Molded | % | ISO 527-2/508 | ||
| Tensile Strength(Break) | Compression Molded | MPa | ASTM D-638 | 22.5 |
| Compression Molded | MPa | ISO 527-2/508 | 22.5 | |
| Tensile Elongation (Break MD) | 50.8um | % | ASTM D-882 | 400 |
| 50.8um | % | ISO 527-3 | 400 | |
| Tensile Elongation (Break TD) | 50.8um | % | ISO 527-3 | 470 |
| 50.8um | % | ASTM D-882 | 470 | |
| Elmendorf Tear Strength (TD) | 50.8um | N | ISO 6383-2 | 2300 |
| 50.8um | g | ASTM D-1922 | 510 | |
| Elmendorf Tear Strength (MD) | 50.8um | g | ASTM D-1922 | 380 |
| 50.8um | N | ISO 6383-2 | 1700 | |
| Tensile Strength (Break TD) | 50.8um | MPa | ASTM D-882 | 38.1 |
| 50.8um | MPa | ISO 527-3 | 38.1 | |
| 50.8um | MPa | ASTM D-882 | 37.9 | |
| 50.8um | MPa | ISO 527-3 | 37.9 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature (DSC) | 内部方法 | 97.8 | °C | |
| Melting temperature | ℃ | Internal Method | 97.8 | |
| Vicat Softening Temperature | ASTMD1525,ISO306 | 81.1 | °C | |
| ℃ | ASTM D-1525 | 81.1 | ||
| ℃ | ISO 306 | 81.1 |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation | MD:断裂,51µm | ASTMD882,ISO527-3 | 400 | % |
| TD:断裂,51µm | ASTMD882,ISO527-3 | 470 | % | |
| Tensile Strength | MD:屈服,51µm | ASTMD882 | 11.8 | Mpa |
| TD:屈服,51µm | ASTMD882 | 10.9 | Mpa | |
| MD:屈服,51µm | ISO527-3 | 11.8 | Mpa | |
| TD:屈服,51µm | ISO527-3 | 10.9 | Mpa | |
| MD:断裂,51µm | ASTMD882,ISO527-3 | 37.9 | Mpa | |
| TD:断裂,51µm | ASTMD882,ISO527-3 | 38.1 | Mpa | |
| Gardner Impact | 51µm | ASTMD1709B,ISO7765-1/B | 580 | g |
| Elmendorf Tear Strength | MD:51µm | ASTMD1922 | 380 | g |
| TD:51µm | ASTMD1922 | 510 | g | |
| MD:51µm | ISO6383-2 | 1700 | N | |
| TD:51µm | ISO6383-2 | 2300 | N |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Gloss | 45°，50.8um | ASTM D-2457 | ||
| 45°,50.8µm | ASTMD2457 | 65 | ||
| Haze | 50.8um | % | ISO 14782 | |
| 50.8um | % | ASTM D-1003 | ||
| 50.8µm | ASTMD1003 | 5.8 | % | |
| 50.8µm | ISO14782 | 5.8 | % |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| monomer Content | % | Internal Method | ||
| Melt Mass-Flow Rate | 190℃/2.16kg | g/10min | ASTM D-1238 | 1.5 |
| 190℃/2.16kg | g/10min | ISO 1133 | 1.5 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.