PPA AMODEL® A-4422 WH118 SOLVAY USA
186
- Properties:Chemical resistanceLow moisture absorption
- Usages:Vehicle electronicsShell
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD | ASTMD955 | 0.50 | % |
| TD | ASTMD955 | 0.60 | % | |
| Moisture Absorption | 24hr | ASTMD570 | 0.20 | % |
| Density / Specific Gravity | ISO1183/A | 1.60 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | ISO527-2 | 9100 | Mpa | |
| Flexural Modulus | ISO178 | 7790 | Mpa | |
| Tensile Strength | ASTMD638 | 102 | Mpa | |
| Flexural Stress | ISO178 | 171 | Mpa | |
| Tensile Strain | 断裂 | ISO527-2 | 1.3 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear thermal expansion coefficient | MD：50到100°C | ASTME831 | 3.1E-05 | cm/cm/°C |
| MD：100到150°C | ASTME831 | 3.8E-05 | cm/cm/°C | |
| MD：150to200°C | ASTME831 | 2.7E-05 | cm/cm/°C | |
| MD：200to250°C | ASTME831 | 3.1E-05 | cm/cm/°C | |
| TD：50到100°C | ASTME831 | 6.3E-05 | cm/cm/°C | |
| TD：100到150°C | ASTME831 | 1E-04 | cm/cm/°C | |
| TD：150to200°C | ASTME831 | 1.3E-04 | cm/cm/°C | |
| TD：200to250°C | ASTME831 | 1.5E-04 | cm/cm/°C | |
| Melting temperature | ISO11357-3 | 324 | °C | |
| Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO75-2/B | 306 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | ISO180/1A | 2.9 | kJ/m² |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| --2 | ASTME1331 | >90 | % | |
| --3 | ASTME1331 | >90 | % | |
| --4 | ASTME1331 | >90 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.