| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 10.8 | kg·cm/cm(J/M)ft·lb/in |
| Modeling Shrinkage | | ASTM D955 | 0.3-0.7 | % |
| Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.2 | % |
| Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 12 | g/10min |
| Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 10 | g/10min |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | | | 0.2 | % |
| Index of Refraction | | | 1.569 | |
| | | 220-240 | °C |
| | | 220-270 | °C |
| | | 40-80 | °C |
| Melt index | 200/21 6 | | 12 | |
| Melt index | 220/10 | | 10 | |
| Modeling Shrinkage | | | 0.3-0.7 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy impact strength | +23/-40℃ | | 18/18 | KJ/m |
| Tensile Modulus | | | 3800 | Mpa |
| Tensile Creep Modulus | 1000h 伸长率＜＝0.5%+23℃ | | 2800 | Mpa |
| Tensile Elongation | | | 3 | % |
| Rockwell Hardness | | ASTM D785 | 83 | |
| Rockwell Hardness | | | 83 | M |
| | | 125 | Mpa |
| Tensile Stress(Break) | | | 75 | Mpa |
| Charpy Notched Impact Strength | 23℃ | | 2 | KJ/m |
| Notched Izod Impact Strength | 23℃ | | 2 | KJ/m |
| Ball Indentation Hardness | | | 165 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Continuous Use Temperature | | | 85 | °C |
| Dielectric Strength | | | 0.17 | W/K.m |
| Deflection Temperature Under Load? | 0.45MPa(HDT B) | | 102 | °C |
| Deflection Temperature Under Load? | 1.8MPa(HDT A) | | 98 | °C |
| Melting Temperature | | | 85 | ℃（℉） |
| Vicat Softening Temperature | | ASTM D1525/ISO R306 | 106 | ℃（℉） |
| Vicat Softening Temperature | | | 106 | °C |
| Linear expansion coefficient | 纵向(23-80)℃ | | 7 | |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | 7 | mm/mm.℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | K20/P20 | | 95 | KV/mm |
| Volume Resistivity | | | 10 | Ω.cm |
| Comparative Tracking Index | 试验溶液A/CTIM | | CTI 425 | |
| Comparative Tracking Index | 试验溶液B | | CTI 200M | |
| Surface resistance | | | 10 | Ω |
| Taber Abrasion Resistance | 100Hz/1MHz | | 0.004/0.007 | |
| Dielectric Constant | 100Hz/1MHz | | 3/2.7 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.