Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD | ASTMD955 | 0.40to0.60 | % |
| Modeling Shrinkage | | ISO2577 | 0.40to0.60 | % |
| Melt Mass-Flow Rate | 260°C/5.0kg | ASTMD1238 | 20 | g/10min |
| Melt Mass-Flow Rate | 260°C/5.0kg | ISO1133 | 20 | g/10min |
| | 内部方法 | 28.0 | CM |
| Density/Specific Gravity 2 | | ASTMD792 | 1.15 | g/cm³ |
| Density / Specific Gravity | 23°C | ISO1183 | 1.15 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Modulus | 23°C | ASTMD790 | 2300 | Mpa |
| Tensile Strain | Break,23°C | ASTMD638 | 90 | % |
| Flexural Modulus | | ISO178 | 2300 | Mpa |
| Flexural Strength | 23°C | ASTMD790 | 78.5 | Mpa |
| Tensile Strength | Yield,23°C | ASTMD638 | 53.0 | Mpa |
| Flexural Stress | | ISO178 | 85.0 | Mpa |
| Tensile Stress | 屈服 | ISO527-2/50 | 55.0 | Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 57.0 | Mpa |
| Tensile Strain | 断裂 | ISO527-2/50 | 130 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 7.5E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | MD：23到55°C | ISO11359-2 | 7.5E-05 | cm/cm/°C |
| Vicat Softening Temperature | -- | ASTMD152510 | 140 | °C |
| Vicat Softening Temperature | -- | ASTMD152511 | 133 | °C |
| Vicat Softening Temperature | -- | ISO306/A50 | 140 | °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 125 | °C |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 110 | °C |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 118 | °C |
| Heat Deflection Temperature | 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 108 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | IEC60093 | 1E+16 | ohms |
| Dielectric Constant | 1MHz | IEC60250 | 3.00 | |
| Volume Resistivity | | IEC60093 | 1E+18 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | -30°C,3.18mm | ASTMD256 | 490 | J/m |
| Notched Izod Impact Strength | 23°C,3.18mm | ASTMD256 | 590 | J/m |
| Notched Izod Impact Strength | -30°C | ISO180 | 45 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180 | 55 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179 | 45 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179 | 55 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R计秤,23°C | ASTMD785 | 114 | |
| Rockwell Hardness | R计秤,23°C | ISO2039-2 | 114 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.