TPE Hytrel® 5526 DUPONT USA

194

Properties:
Weather resistance
UV resistance
High mobility
Thermal stability
Usages:
Electrical tools
Electrical field
Electrical appliances
Electronic field
Automotive sector
Certificates:
UL
Compare

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	ISO294-4	1.4	%
Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	1.4	%
Moisture Absorption	23°C,24hr	ISO62	0.60	%
	Moisture Absorption	饱和,23°C,2.00mm	ISO62	0.60	%
	Moisture Absorption	Moisture Absorption	平衡,23°C,2.00mm,50%RH	ISO62	0.20	%
Melt Mass-Flow Rate		ISO1133	18	g/10min
MediumDensity			1.04	g/cm³
SpecificHeatCapacityofMelt			2110	J/kg/°C
ThermalConductivityofMelt			0.19	W/m/K
Melt Volume flow Rate	220°C/2.16kg	ISO1133	17.5	cm3/10min
Density / Specific Gravity		ISO1183	1.19	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Nominal Tensile Strain at Break		ISO527-2	780	%
Abrasion Resistance		ISO4649	120	mm³
Tensile Creep Modulus	1000hr	ISO899-1	130	Mpa
Tensile Creep Modulus	Tensile Creep Modulus	1hr	ISO899-1	170	Mpa
Tensile Stress	屈服	ISO527-2	15.0	Mpa
	Tensile Stress	断裂	ISO527-2	40.0	Mpa
		Tensile Stress	5.0%应变	ISO527-2	6.90	Mpa
			Tensile Stress	10%应变	ISO527-2	11.0	Mpa
			Tensile Stress	Tensile Stress	50%应变	ISO527-2	14.0	Mpa
Tensile Strain	屈服	ISO527-2	35	%
Tensile Strain	Tensile Strain	断裂	ISO527-2	>300	%
Tensile Modulus		ISO527-2	190	Mpa
Flexural Modulus		ISO178	200	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,未退火	ISO75-2/B	65.0	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,未退火	ISO75-2/A	45.0	°C
Brittleness Temperature		ISO974	-98.0	°C
Vicat Softening Temperature	--	ISO306/A50	180	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B50	75.0	°C
Glass Transition Temperature		ISO11357-2	-20.0	°C
Melting Temperature		ISO11357-3	203	°C
Linear thermal expansion coefficient	MD：--	ISO11359-2	2E-04	cm/cm/°C
	Linear thermal expansion coefficient	MD：-40to23°C	ISO11359-2	1.8E-04	cm/cm/°C
		Linear thermal expansion coefficient	TD：--	ISO11359-2	2E-04	cm/cm/°C
			Linear thermal expansion coefficient	TD：-40to23°C	ISO11359-2	1.7E-04	cm/cm/°C
			Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：EffectiveThermalDiffusivity	ISO11359-2	9E-08	m²/s

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength		IEC60243-1	20	KV/mm
Dissipation Factor?	1MHz	IEC60250	0.038
Dissipation Factor?	Dissipation Factor?	100Hz	IEC60250	9E-03
Relative Permittivity	1MHz	IEC60250	4.60
Relative Permittivity	Relative Permittivity	100Hz	IEC60250	4.90
Comparative Tracking Index		IEC60112	600	V
Surface Resistivity		IEC60093	>1.0E+15	ohms
Volume Resistivity		IEC60093	4E+13	ohms·cm

Elastomers Properties	Test Condition	Test Method	Test Result	Unit
Tearing Strength	横向流量	ISO34-1	130	kN/m
Tearing Strength	Tearing Strength	流量	ISO34-1	130	kN/m

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-40°C	ISO179/1eA	30	kJ/m²
	Charpy Notched Impact Strength	-30°C,局部断裂	ISO179/1eA	150	kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	NoBreak
Tensile Impact Strength	23°C	ISO8256/1	270	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	NoBreak
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Shore Hardness	邵氏D	ISO868	55
Shore Hardness	Shore Hardness	邵氏D,15秒	ISO868	51

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	3.0mm	IEC60695-11-10,-20	HB
	UL flame retardant rating	1.5mm	IEC60695-11-10,-20	HB
		UL flame retardant rating	3.0mm	UL94	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	UL94	HB
Oxygen Index		ISO4589-2	21	%
FMVSS Flammability		FMVSS302	SE/B
Fogging-G-value	condensate	ISO6452	1E-04	g
Burning Rate	1.00mm	ISO3795	28	mm/min

Supplementary information	Test Condition	Test Method	Test Result	Unit
Odor		VDA270	5.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.