Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238,ISO1133 | 9.8 | g/10min |
| monomer Content | | 内部方法 | 8.0 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus (2% Secant) | | ASTMD638,ISO527-2 | 110 | Mpa |
| Tensile Elongation | 断裂 | ASTMD638,ISO527-2 | 570 | % |
| Tensile Strength | 屈服 | ASTMD638,ISO527-2 | 7.00 | Mpa |
| Tensile Strength | 断裂 | ASTMD638,ISO527-2 | 19.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | -- | ASTMD1525 | 82.2 | °C |
| Vicat Softening Temperature | -- | ISO306 | 82.0 | °C |
| Melting temperature (DSC) | | 内部方法 | 100 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Peak Melting Temperature | | 内部方法 | 85.0 | °C |
| Water Vapor Transmission Rate | 38°C,90%RH | DIN53122/2 | 0.40 | g·mm/m²/atm/24hr |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | 邵氏D | ASTMD2240,ISO868 | 53 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.