Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 200°C/5.0 kg | ASTM D1238, ISO 1133 | 2.3 | g/10 min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | 23°C | ASTM D638, ISO 527-2 | 3040 | Mpa |
| Tensile Elongation | 断裂, 23°C | ASTM D638, ISO 527-2 | 2.0 | % |
| Flexural Modulus | 23°C | ASTM D790, ISO 178 | 3330 | Mpa |
| Flexural Strength | 23°C | ASTM D790, ISO 178 | 98.0 | Mpa |
| Tensile Strength | 23°C | ASTM D638, ISO 527-2 | 51.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ASTM D1525, ISO 306 | 104 | °C |
| Deflection Temperature Under Load? | 1.8 MPa, 退火, 3.18 mm | ASTM D648, ISO 75-2/A | 95.0 | °C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Time | | | 1.0 到 2.0 | hr |
| Rear Temperature | | | 195 | °C |
| Middle Temperature | | | 210 到 220 | °C |
| Front Temperature | | | 215 | °C |
| Hopper Temperature | | | 40 | °C |
| Drying Temperature | | | 75 | °C |
| Processing (Melt) Temp | | | 190 到 230 | °C |
| Mold Temperature | | | 20 到 70 | °C |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Residual monomer | | | < 700 | ppm |
| Flame Rating | 1.5 mm, NC | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices