Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 23°C,24hr,3.20mm | ISO62 | 0.060 | % |
| Moisture Absorption | 平衡,23°C,3.20mm,50%RH | ISO62 | 0.40 | % |
| Density / Specific Gravity | | ISO1183 | 1.38 | g/cm³ |
| Spiral Flow | | 内部方法 | 10.0 | CM |
| Modeling Shrinkage | TD:180°C | ISO294-4 | 0.90 | % |
| Modeling Shrinkage | MD:180°C | ISO294-4 | 0.50 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Stress | 23°C | ISO178 | 240 | Mpa |
| Compressive Stress | 23°C | ISO604 | 200 | Mpa |
| Compressive Stress | 120°C | ISO604 | 130 | Mpa |
| Compressive Stress | 200°C | ISO604 | 40.0 | Mpa |
| Tensile Stress | 断裂,23°C | ISO527-2 | 140 | Mpa |
| Tensile Stress | 断裂,125°C | ISO527-2 | 80.0 | Mpa |
| Tensile Stress | 断裂,175°C | ISO527-2 | 45.0 | Mpa |
| Tensile Stress | 断裂,275°C | ISO527-2 | 25.0 | Mpa |
| Tensile Strain | 断裂,23°C | ISO527-2 | 4.0 | % |
| Tensile Modulus | 23°C | ISO527-2 | 7500 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 7000 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/Af | 298 | °C |
| Linear thermal expansion coefficient | MD:<143°C | ISO11359-2 | 2.5E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | MD:>143°C | ISO11359-2 | 3E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD:<143°C | ISO11359-2 | 5E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD:>143°C | ISO11359-2 | 1.3E-04 | cm/cm/°C |
| Melting temperature | | ISO11357-3 | 343 | °C |
| Glass Transition Temperature | | ISO11357-2 | 143 | °C |
| Specific Heat | 23°C | DSC | 1700 | J/kg/°C |
| Thermal Conductivity | 23°C | ISO22007-4 | 0.30 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | 2.00mm | IEC60243-1 | 24 | KV/mm |
| Dissipation Factor? | 23°C,1MHz | IEC60250 | 5E-03 | |
| Comparative Tracking Index | | IEC60112 | 150 | V |
| Dielectric Constant | 23°C,1kHz | IEC60250 | 3.10 | |
| Volume Resistivity | | IEC60093 | 1E+16 | ohms·cm |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Viscosity | 400°C | ISO11443 | 450 | Pa·s |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179/1U | 60 | kJ/m² |
| Notched Izod impact strength | 23°C | ISO180 | 55 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 5.5 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/A | 6.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | 邵氏D,23°C | ISO868 | 86 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.