Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD2.0mm | ISO294-4 | 0.65 | % |
| Melt Mass-Flow Rate | 220℃/10Kg | ISO1133 | 22.00 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 11 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 4.0 | kJ/m² |
| Tensile Modulus | 23°C | ISO527-2 | 2600 | Mpa |
| Tensile Strength | 23°C | ISO527-2 | 50 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 2700 | Mpa |
| Flexural Strength | 23°C | ISO178 | 80 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.80MPa退火 | ISO75-2/Af | 83 | °C |
| Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Insulation strength | | IEC60243-1 | 32 | KV/mm |
| Volume Resistivity | | IEC60093 | 1E+15 | Ω.cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | | ISO2039-2 | 110 | R |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.