Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 125°C/2.16kg2 | ASTMD1238,ISO1133 | 14 | g/10min |
| Melt Mass-Flow Rate | 190°C/2.16kg3 | ASTMD1238,ISO1133 | 300 | g/10min |
| monomer Content | | 内部方法 | 20.5 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus (2% Secant) | 模压成型 | ASTMD638,ISO527-2 | 33.1 | Mpa |
| Tensile Strength | 断裂,模压成型 | ASTMD638,ISO527-2 | 9.65 | Mpa |
| Tensile Elongation?(Break) | Compression Molded | % | ASTM D-638 | 390 |
| Tensile Elongation?(Break) | Compression Molded | % | ISO 527-2 | 390 |
| Tensile Elongation | 断裂,模压成型 | ASTMD638,ISO527-2 | 390 | % |
| Tensile Strength(Break) | Compression Molded | MPa | ASTM D-638 | 9.65 |
| Tensile Strength(Break) | Compression Molded | MPa | ISO 527-2 | 9.65 |
| Shore Hardness | Shore D | | ASTM D-2240 | |
| Shore Hardness | Shore D | | ISO 868 | |
| Tensile Modulus (2% Secant) | Compression Molded | MPa | ASTM D-638 | 33.1 |
| Tensile Modulus (2% Secant) | Compression Molded | MPa | ISO 527-2 | 33.1 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ℃ | ASTM D-1525 | 42.2 |
| Vicat Softening Temperature | | ℃ | ISO 306 | 42.2 |
| Melting temperature (DSC) | | 内部方法 | 77.2 | °C |
| Melting temperature | | ℃ | Internal Method | 77.2 |
| Vicat Softening Temperature | | ASTMD1525,ISO306 | 42.2 | °C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | 邵氏D | ASTMD2240,ISO868 | 50 | |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| monomer Content | | % | Internal Method | 20.5 |
| Melt index | 125℃/2.16kg | g/10min | ASTM D-1238 | |
| Melt index | 190℃/2.16kg | g/10min | ISO 1133 | 300 |
| Melt index | 190℃/2.16kg | g/10min | ASTM D-1238 | 300 |
| Melt index | 125℃/2.16kg | g/10min | ISO 1133 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.