Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density / Specific Gravity | 23℃/23℃ | ASTM D-792(ISO 1183) | 1.04 | |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| flexural modulus | 23℃ | ASTM D-790(ISO 178) | 25000(2450) | kg/cm2(MPa) |
| Tensile Strength | 23℃ | ASTM D-638(ISO 527) | 490(48) | kg/cm2(MPa) |
| Rockwell Hardness | 23℃ | ASTM D-785(ISO 2039/2) | R-102 | |
| Flexural Strength | 23℃ | ASTM D-790(ISO 178) | 740(73) | kg/cm2(MPa) |
| Izod Impact Strength | 23℃1/4"厚 | ASTM D-256(ISO R180) | 46(451) | kg.cm/cm(J/m) |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | Unanneaied 18.6kg/cm²(1/2"厚） | ASTM D-648(ISO 75/A) | 92 | °C |
| Deflection Temperature Under Load? | Annealed(8℃×8hr) | ASTM D-648(ISO 75/A) | 104 | °C |
| Vicat Softening Temperature | 1Kg load | ASTM D-1525(ISO 306) | 107 | °C |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 220℃×10kgf(98N) | ASTM D-1238(ISO 1133) | 6.5 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.