Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | | ISO294-4 | 0.30to0.70 | % |
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.30 | % |
| Apparent Density | | | 0.60 | g/cm³ |
| Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 7.00 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | 屈服,23°C | ISO527-2 | 79.0 | Mpa |
| Tensile Strain | 断裂,23°C | ISO527-2 | 3.0 | % |
| Tensile Modulus | | ISO527-2 | 3900 | Mpa |
| Flexural Stress | | ISO178 | 135 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 0.45MPa,Annealed | ISO75-2/B | 110 | °C |
| Heat Deflection Temperature | 1.8MPa,Annealed | ISO75-2/A | 104 | °C |
| Thermal Conductivity | | DIN52612 | 0.17 | W/m/K |
| Vicat Softening Temperature | | ISO306/B50 | 120 | °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation Factor? | 100Hz | IEC60250 | 5E-03 | |
| Dissipation Factor? | 1MHz | IEC60250 | 7E-03 | |
| Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
| Dielectric Constant | 100Hz | IEC60250 | 3.00 | |
| Volume Resistivity | | IEC60093 | 1E+16 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179 | 21 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 20 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M级 | | 84 | |
| Ball Indentation Hardness | | ISO2039-1 | 175 | Mpa |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index of light | | ISO489 | 1.567 | |
| Transmittance | 550nm | ASTMD1003 | >89.0 | % |
| Haze | | ASTMD1003 | <1.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.