Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1040 | |
| Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 10 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | 50mm/min | ISO 178/1993 | 80 | Mpa |
| Tensile Strength(Yield) | | ISO 572-2/1993 | 50 | Mpa |
| Tensile Modulus | 2mm/min | ISO 178/1993 | 3200 | Mpa |
| Charpy Notched Impact Strength | | ISO 179/1993 | 10 | KJ/m |
| Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 2 | % |
| Tensile Elongation | | ASTM D638/ISO 527 | 50 | % |
| Tensile Elongation | 50mm/min | ISO 572-2/1993 | 2 | % |
| Flexural Modulus | | ASTM D790/ISO 178 | 3200 | kg/cm²(MPa)[Lb/in²] |
| Flexural Strength | | ASTM D790/ISO 178 | 80 | kg/cm²(MPa)[Lb/in²] |
| Charpy impact strength | | ASTM D256/ISO 179 | 10 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 78 | ℃（℉） |
| Deflection Temperature Under Load? | 1.82MPa | ISO 75-2/1993 | 78 | °C |
| Vicat Softening Temperature | B50/oil | ISO 306/1994 | 88 | °C |
| Vicat Softening Temperature | | ASTM D1525/ISO R306 | 88 | ℃（℉） |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 200℃/5Kg | ISO 1133/1997 | 10 | g/10min |
| Density | | ISO 1183/1997 | 1040 | kg/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare