Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 200℃×5kgf(49N) | ASTM D-1238(ISO 1133) | 7.0 | g/10min |
| Modeling Shrinkage | 23℃ | ISO 622 | 0.3-0.5 | |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | 23℃ | ASTM D-638(ISO 527) | 420(41) | kg/cm2(MPa) |
| Tensile Elongation | 23℃ | ASTM D-638(ISO 527) | 2.1 | |
| Flexural Strength | 23℃ | ASTM D-790(ISO 178) | 800(78) | kg/cm2(MPa) |
| flexural modulus | 23℃ | ASTM D-790(ISO 178) | 3.4(3330) | kg/m2*104(MPa) |
| Tensile Modulus | 23℃ | ASTM D-638(ISO 527) | 1.8(1770) | kg/cm2*104(MPa) |
| Izod Impact Strength | 23℃，1/4” | ASTM D-256(ISO R180) | 1.8(18) | kg.cm/cm(J/m) |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flammability | FILE NOE162823,1/16" | UL 94 | HB | |
| Deflection Temperature Under Load? | Annealed(80℃×2Hr1/8"厚) | ASTM D-648(ISO 75/A) | 88 | °C |
| Vicat Softening Temperature | Annealed(80℃×2Hr1/8"厚) | ASTM D-1525(ISO 306B) | 93 | |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|
| monomer Content | | | 700 | ppm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare