Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | 横向流量 | ISO 294-4 | 1.3 | % |
| Modeling Shrinkage | 流量 | ISO 294-4 | 0.50 | % |
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 2.6 | % |
| Density | | ISO 1183 | 1.41 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | 断裂 | ISO 527-2 | 210 | Mpa |
| Tensile Stress | 断裂, 120°C | ISO 527-2 | 110 | Mpa |
| Tensile Stress | 断裂, 160°C | ISO 527-2 | 100 | Mpa |
| Tensile Stress | 断裂, 180°C | ISO 527-2 | 95.0 | Mpa |
| Tensile Stress | 断裂, 200°C | ISO 527-2 | 90.0 | Mpa |
| Tensile Strain | 断裂 | ISO 527-2 | 4.0 | % |
| Tensile Strain | 断裂, 120°C | ISO 527-2 | 7.5 | % |
| Tensile Strain | 断裂, 160°C | ISO 527-2 | 7.5 | % |
| Tensile Strain | 断裂, 180°C | ISO 527-2 | 7.5 | % |
| Tensile Strain | 断裂, 200°C | ISO 527-2 | 7.5 | % |
| Tensile Modulus | -- | ISO 527-2 | 10000 | Mpa |
| Tensile Modulus | 120°C | ISO 527-2 | 5500 | Mpa |
| Tensile Modulus | 160°C | ISO 527-2 | 5000 | Mpa |
| Tensile Modulus | 180°C | ISO 527-2 | 4400 | Mpa |
| Tensile Modulus | 200°C | ISO 527-2 | 4000 | Mpa |
| Flexural Modulus | -- | ISO 178 | 9000 | Mpa |
| Flexural Modulus | 120°C | ISO 178 | 4700 | Mpa |
| Flexural Modulus | 160°C | ISO 178 | 3900 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45 MPa, 未退火 | ISO 75-2/B | 290 | °C |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火 | ISO 75-2/A | 290 | °C |
| Melting Temperature | | ISO 11357-3 | 295 | °C |
| Linear thermal expansion coefficient | 流动 | ISO 11359-2 | 2.5E-5 | cm/cm/°C |
| Linear thermal expansion coefficient | 横向 | ISO 11359-2 | 6.0E-5 | cm/cm/°C |
| | IEC 60216 | 159 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | | IEC 60243-1 | 35 | KV/mm |
| Relative Permittivity | 100 Hz | IEC 60250 | 4.40 | |
| Relative Permittivity | 1 MHz | IEC 60250 | 4.00 | |
| Relative Permittivity | 1.00 GHz | IEC 60250 | 3.60 | |
| Comparative Tracking Index | | IEC 60112 | 500 | V |
| Volume Resistivity | | IEC 60093 | 1.0E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 65 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 80 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 11 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 | kJ/m² |
| Notched Izod Impact Strength | -40°C | ISO 180/1A | 11 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO 180/1A | 12 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flammability level | 0.9 mm | IEC 60695-11-10, -20 | HB | |
| Flammability level | 1.6 mm | IEC 60695-11-10, -20 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.