Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 24 hr | ASTM D570 | 0.25 | % |
| Moisture Absorption | 平衡, 23°C | ASTM D570 | 1.3 | % |
| Melt Mass-Flow Rate | 337°C/6.6 kg | ASTM D1238 | 18 | g/10 min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ASTM D638 | 3580 | Mpa |
| Tensile Elongation | 屈服 | ASTM D638 | 7.0 | % |
| Tensile Elongation | 断裂 | ASTM D638 | 60 | % |
| Flexural Modulus | 100 mm 跨距 | ASTM D790 | 3510 | Mpa |
| Flexural Strength | 屈服, 100 mm 跨距 | ASTM D790 | 165 | Mpa |
| Taber Abrasion Resistance | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 10.0 | mg |
| Tensile Strength | 屈服 | ASTM D638 | 110 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ASTM D15255 | 218 | °C |
| Thermal Conductivity | | ASTM C177 | 0.22 | W/m/K |
| RTI | | UL 746 | 170 | °C |
| RTI Imp | | UL 746 | 170 | °C |
| RTI Elec | | UL 746 | 170 | °C |
| Coefficient of Linear Thermal Expansion (Flow) | -20 到 150°C | ASTM E831 | 5.6E-5 | cm/cm/°C |
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 207 | °C |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 198 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Comparative Tracking Index | | UL 746 | PLC 4 | |
| High Amp Arc Ignition | | UL 746 | PLC 3 | |
| Hot-wire Ignition | | UL 746 | PLC 1 | |
| Dielectric Constant | 1 kHz | ASTM D150 | 3.15 | |
| Volume Resistivity | | ASTM D257 | 1.0E+17 | ohms·cm |
| Dissipation Factor? | 1 kHz | ASTM D150 | 1.3E-3 | |
| Dissipation Factor? | 2.45 GHz | ASTM D150 | 2.5E-3 | |
| Dielectric Strength | 1.60 mm, in Air | ASTM D149 | 33 | KV/mm |
| Dielectric Strength | 1.60 mm, in Oil | ASTM D149 | 28 | KV/mm |
| High Voltage Arc Tracking Rate | | UL 746 | PLC 2 | |
| Arc Resistance | | ASTM D495 | PLC 5 | |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Temperature | | | 150 | °C |
| Suggested Max Moisture | | | 0.020 | % |
| Processing (Melt) Temp | | | 350 到 400 | °C |
| Mold Temperature | | | 135 到 165 | °C |
| Drying Time | | | 4.0 到 6.0 | hr |
| Suggested Shot Size | | | 40 到 60 | % |
| Rear Temperature | | | 330 到 400 | °C |
| Middle Temperature | | | 340 到 400 | °C |
| Front Temperature | | | 345 到 400 | °C |
| Nozzle Temperature | | | 345 到 400 | °C |
| Back Pressure | | | 0.300 到 0.700 | Mpa |
| Screw Speed | | | 40 到 70 | rpm |
| Vent Depth | | | 0.025 到 0.076 | mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Reverse Notch Izod Impact | 3.20 mm | ASTM D256 | 1200 | J/m |
| Gardner Impact | 23°C | ASTM D3029 | 33.0 | J |
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 1300 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M 级 | ASTM D785 | 109 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Oxygen Index | | ASTM D2863 | 44 | % |
| Flame Rating | 0.75 mm | UL 94 | V-0 | |
| Flame Rating | 3.0 mm | UL 94 | 5VA | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.