PPO NORYL™ GFN2 SABIC INNOVATIVE US
223
- Properties:enhanceGlass fiber reinforcedGlass fiber reinforced
- Usages:Electrical toolsHousehold appliancesHousehold appliancesAutomotive interior parts
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.20to0.50 | % |
| Moisture Absorption | 24hr | ASTMD570 | 0.060 | % |
| Melt Mass-Flow Rate | 300°C/5.0kg | ASTMD1238 | 9.0 | g/10min |
| Melt Volume flow Rate | 300°C/5.0kg | ISO1133 | 8.10 | cm3/10min |
| Outdoor Suitability | UL746C | f1 | ||
| Density / Specific Gravity | ASTMD792 | 1.20 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Strength | ISO178 | 167 | Mpa | |
| Flexural Modulus | ISO178 | 6540 | Mpa | |
| Tensile Elongation | 断裂 | ASTMD638 | 2.6 | % |
| Tensile Modulus | ASTMD638 | 6200 | Mpa | |
| Tensile Strength | 断裂 | ASTMD638 | 90.0 | Mpa |
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 5800 | Mpa |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 160 | Mpa |
| Tensile Stress | 断裂 | ISO527-2/5 | 97.3 | Mpa |
| Tensile Strain | 断裂 | ISO527-2/5 | 2.5 | % |
| Tensile Modulus | ISO527-2/1 | 7070 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8MPa,未退火,3.20mm | ASTMD648 | 135 | °C |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 138 | °C | |
| 0.45MPa,未退火,3.20mm | ASTMD648 | 141 | °C | |
| 0.45MPa,未退火,6.40mm | ASTMD648 | 143 | °C | |
| Vicat Softening Temperature | -- | ISO306/B50 | 143 | °C |
| -- | ISO306/B120 | 146 | °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 2.9E-05 | cm/cm/°C |
| TD：-40到40°C | ASTME831 | 8.3E-05 | cm/cm/°C | |
| RTIElec | UL746 | 90.0 | °C | |
| Evolution Calendar intelligent importer | UL746 | 90.0 | °C | |
| RTIStr | UL746 | 90.0 | °C | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 137 | °C |
| 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 143 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Arc Resistance | ASTMD495 | PLC7 | ||
| High Amp Arc Ignition | HAI | UL746 | PLC4 | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC4 | |
| Hot-wire Ignition | HWI | UL746 | PLC4 | |
| Dissipation Factor? | 50Hz | ASTMD150 | 8E-04 | |
| 60Hz | ASTMD150 | 8E-04 | ||
| Dielectric Strength | 3.20mm,inOil | ASTMD149 | 17 | KV/mm |
| Dielectric Constant | 50Hz | ASTMD150 | 2.86 | |
| 60Hz | ASTMD150 | 2.86 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 22.6 | J |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 11 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/2C | 12 | kJ/m² |
| Notched Izod Impact Strength | -40°C | ASTMD256 | 96 | J/m |
| 23°C | ASTMD256 | 120 | J/m | |
| 23°C | ASTMD4812 | 650 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | L计秤 | ASTMD785 | 106 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen Index | ASTMD2863 | 26 | % | |
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.