Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD：3.20mm | ASTMD955 | 0.50to0.70 | % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 11 | g/10min |
| Density / Specific Gravity | | ASTMD792 | 1.21 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Strength | 屈服,3.20mm | ASTMD790 | 98.1 | Mpa |
| Flexural Modulus | 3.20mm | ASTMD790 | 2260 | Mpa |
| Tensile Strength | 屈服,3.20mm | ASTMD638 | 61.8 | Mpa |
| Tensile Elongation | 断裂,3.20mm | ASTMD638 | >150 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| RTIElec | | UL746 | 120 | °C |
| Evolution Calendar intelligent importer | | UL746 | 110 | °C |
| RTIStr | | UL746 | 120 | °C |
| Vicat Softening Temperature | | ASTMD15255 | 141 | °C |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 130 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | 23°C,3.20mm | ASTMD256 | 780 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R级 | ASTMD785 | 118 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.0mm | UL94 | V-0 | |
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| UL flame retardant rating | 2.5mm | UL94 | V-05VA | |
| UL flame retardant rating | 3.0mm | UL94 | V-05VA | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.