| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | | | | % |
| Rockwell Hardness | | ASTM D-758(M级) | 97 | |
| Transmittance | | ASTM D-1003 | 92 | % |
| Index of Refraction | | ASTM D-542 | 1.49 | |
| Density / Specific Gravity | | ASTM D-792 | 1.19 | |
| Modeling Shrinkage | (冷模/冷件),48hrs | ASTM D-935 | 0.2-0.6 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact Strength | Izod 研磨缺口 | ASTM D256 | 1.2(12.3) | kgf-cm/cm(J/m) |
| Impact Strength | 落锤(15.2×15.2×0.3cm重1.4kg半径0.64cm) | ASTM D256 | 14(1.4) | kg-cm(J) |
| flexural modulus | | ASTM D-790 | 32000 | Kgf/cm |
| Tensile Strength | 初级应变速度0.1cm/cm/min | ASTM D-638 | 720(70) | Kgf/cm |
| Flexural Strength | 横跨比=16 | ASTM D-790 | 1050(103) | Kgf/cm |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | 50℃/hr,1kg | ASTM D-1525，未退火 | 111 | °C |
| Vicat Softening Temperature | 50℃/hr,5kg | ASTM D-1525，未退火 | 104 | °C |
| Glass Transition Temperature | Tg | | 108 | °C |
| Use Temperature | 与残余应力大小有关 | | 85-102 | °C |
| Deflection Temperature Under Load (Annealed) | 2℃/min,18.6kgf/cm | ASTM D-648 | 102 | °C |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 浸水24hrs后增重 | ASTM D-570 | 0.3 | % |
| Melt index | | ASTM D-1238 | 3.5 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.