ASA/PC GELOY™ XP4034 BK SABIC INNOVATIVE US
450
- Properties:Thermal stabilityHigh mobilityAntistaticWeather resistance
- Usages:Automotive sector
- Certificates:UL
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Modeling Shrinkage | 流动 : 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
横向流动 : 3.20 mm | 内部方法 | 0.50 到 0.70 | % | |
Moisture Absorption | 24 hr | ASTM D570 | 0.25 | % |
Melt Mass-Flow Rate | 220°C/10.0 kg | ASTM D1238 | 5.0 | g/10 min |
260°C/5.0 kg | ASTM D1238 | 14 | g/10 min | |
280°C/3.8 kg | ASTM D1238 | 24 | g/10 min | |
Outdoor Suitability | UL 746C | f2 |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Tensile Strain | 屈服 | ISO 527-2/50 | 4.5 | % |
断裂 2 | ASTM D638 | 25 | % | |
断裂 | ISO 527-2/50 | 130 | % | |
Tensile Modulus | ISO 527-2/1 | 2500 | Mpa | |
Flexural Modulus | 50.0 mm 跨距 3 | ASTM D790 | 2510 | Mpa |
-- 4 | ISO 178 | 2500 | Mpa | |
Tensile Strength | 屈服 2 | ASTM D638 | 62.0 | Mpa |
屈服 | ISO 527-2/50 | 57.0 | Mpa | |
断裂 | ISO 527-2/50 | 50.0 | Mpa | |
Flexural Stress | -- 4, 5 | ISO 178 | 75.0 | Mpa |
屈服, 50.0 mm 跨距 3 | ASTM D790 | 88.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Thermal Conductivity | ASTM C177 | 0.25 | W/m/K | |
Vicat Softening Temperature | ISO 306/B50 | 113 | °C | |
Linear thermal expansion coefficient | 流动 : -20 到 150°C | ASTM E831 | 7.2E-5 | cm/cm/°C |
横向 : -20 到 150°C | ASTM E831 | 7.2E-5 | cm/cm/°C | |
Deflection Temperature Under Load? | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 115 | °C |
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7 | ISO 75-2/Bf | 116 | °C | |
1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 104 | °C | |
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7 | ISO 75-2/Af | 98.0 | °C |
Injection | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Drying Time | 3.0 到 4.0 | hr | ||
Suggested Shot Size | 40 到 80 | % | ||
Rear Temperature | 240 到 255 | °C | ||
Middle Temperature | 245 到 260 | °C | ||
Front Temperature | 250 到 265 | °C | ||
Nozzle Temperature | 245 到 265 | °C | ||
Back Pressure | 0.300 到 1.00 | Mpa | ||
Screw Speed | 30 到 80 | rpm | ||
Vent Depth | 0.038 到 0.076 | mm | ||
Drying Temperature | 95 到 105 | °C | ||
Suggested Max Moisture | 0.040 | % | ||
Processing (Melt) Temp | 260 到 275 | °C | ||
Mold Temperature | 55 到 70 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Instrumented Dart Impact | -30°C, Total Energy | ASTM D3763 | 30.0 | J |
23°C, Total Energy | ASTM D3763 | 47.0 | J |
hardness | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Rockwell Hardness | R 级 | ASTM D785 | 110 |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Gardner | 60°, 无织构 | ASTM D523 | 94 |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Flame Rating | 1.5 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.