Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | 23℃ | ISO 1183 | 1.06 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched | ISO 179/2C | 3 | kJ/m² |
| Unnotched | ISO 179/2D | 15 | kJ/m² |
| 50 mm/min,yield | ISO 527 | 52 | Mpa |
| 50 mm/min,break | ISO 527 | 52 | Mpa |
| 2 mm/min | ISO 178 | 2.6 | GPa |
| hardness | H358/30 | ISO 2039-1 | 155 | n/mm² |
| Tensile Elongation | 50 mm/min | ISO 527 | 4 | % |
| Flexural Strength | 2 mm/min | ISO 178 | 178 | Mpa |
| Notched Izod Impact Strength | Notched | ISO 180/1A | 2 | kJ/m² |
| Charpy Notched Impact Strength | Notched | ISO 179 | 2 | kJ/m² |
| Charpy Notched Impact Strength | Unnotched | ISO 179 | 18 | kJ/m² |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | 1 Kg,50℃/hr | ISO 306 | 104 | ℃ |
| Heat Deflection Temperature | 1.8 MPa Unannealed | ISO 75 | 88 | ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices