Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 372°C/5.0kg | ASTMD1238 | 10到17 | g/10min |
| Apparent Density | | JISK6891 | 1.00到1.40 | g/cm³ |
| Moisture Absorption | 饱和 | ASTMD570 | <0.010 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation | 断裂 | JISK6891 | 350到450 | % |
| Flexural Modulus | | ASTMD790 | 580到690 | Mpa |
| Tensile Strength | 屈服 | JISK6891 | 25.4到30.4 | Mpa |
| Compressive Strength | 1%应变 | ASTMD695 | 4.90到5.90 | Mpa |
| Compressive Strength | 25%应变 | ASTMD695 | 31.4到33.3 | Mpa |
| Compressive Strength | 摩擦系数(与钢-静态) | ASTMD695 | 0.040到0.050 | |
| Compressive Modulus | | ASTMD695 | 490到590 | Mpa |
| Flexural Strength | | ASTMD790 | Nobreak | |
| Heat Deflection Temperature | 25°C,14MPa3 | ASTMD621 | 8.00到9.00 | % |
| Heat Deflection Temperature | 100°C,6.9MPa2 | ASTMD621 | 2.00到3.00 | % |
| Heat Deflection Temperature | 100°C,6.9MPa3 | ASTMD621 | 8.50到9.50 | % |
| Heat Deflection Temperature | 25°C,14MPa2 | ASTMD621 | 2.50到3.00 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Specific Heat | | | 1050 | J/kg/°C |
| Thermal Conductivity | | ASTMC177 | 0.26 | W/m/K |
| Linear thermal expansion coefficient | MD：20到100°C | ASTMD696 | 1.2E-04 | cm/cm/°C |
| Melting temperature | | ASTMD4591 | 300到310 | °C |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Viscosity | 380°C | | 2.00E+6到2.50E+7 | mPa·s |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | 邵氏D | ASTMD2240 | 60到70 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.6mm | UL94 | V-0 | |
| Oxygen Index | 1.57mm | ASTMD2863 | >95 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.