ASA/PC GELOY™ CR7500-GY SABIC INNOVATIVE US
419
- Properties:Thermal stabilityAntistaticHigh mobility
- Usages:Electrical applicationsAutomotive Applications
Compare
View PricesTechnical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.50 | % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.20 | % | |
| Melt Mass-Flow Rate | 220°C/10.0 kg | ASTM D1238 | 6.3 | g/10 min |
| 260°C/5.0 kg | ASTM D1238 | 11 | g/10 min | |
| Melt Volume flow Rate | 220°C/10.0 kg | ISO 1133 | 6.00 | cm3/10min |
| 260°C/5.0 kg | ISO 1133 | 10.0 | cm3/10min | |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.80 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | -- 5, 6 | ISO 178 | 64.0 | Mpa |
| 屈服, 50.0 mm 跨距 4 | ASTM D790 | 68.0 | Mpa | |
| Tensile Modulus | -- 2 | ASTM D638 | 1970 | Mpa |
| -- | ISO 527-2/1 | 2040 | Mpa | |
| Tensile Elongation | 屈服 3 | ASTM D638 | 3.6 | % |
| 屈服 | ISO 527-2/5 | 3.3 | % | |
| 断裂 3 | ASTM D638 | 60 | % | |
| 断裂 | ISO 527-2/5 | 19 | % | |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2170 | Mpa |
| -- 5 | ISO 178 | 2060 | Mpa | |
| Tensile Strength | 屈服 3 | ASTM D638 | 40.0 | Mpa |
| 屈服 | ISO 527-2/5 | 43.0 | Mpa | |
| 断裂 3 | ASTM D638 | 33.0 | Mpa | |
| 断裂 | ISO 527-2/5 | 35.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | -- | ASTM D152510 | 98.0 | °C |
| -- | ISO 306/B50 | 102 | °C | |
| -- | ISO 306/B120 | 105 | °C | |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 8.4E-5 | cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 9.5E-5 | cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 9.5E-5 | cm/cm/°C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 90.0 | °C |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9 | ISO 75-2/Ae | 88.0 | °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8 | ISO 75-2/Af | 89.0 | °C | |
| Ball PressureTest | 98°C | IEC 60695-10-2 | 通过 |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Time | 3.0 到 4.0 | hr | ||
| Suggested Shot Size | 40 到 80 | % | ||
| Rear Temperature | 230 到 250 | °C | ||
| Middle Temperature | 235 到 255 | °C | ||
| Front Temperature | 245 到 260 | °C | ||
| Nozzle Temperature | 235 到 255 | °C | ||
| Back Pressure | 0.300 到 1.00 | Mpa | ||
| Screw Speed | 30 到 80 | rpm | ||
| Vent Depth | 0.038 到 0.076 | mm | ||
| Drying Temperature | 85 到 95 | °C | ||
| Suggested Max Moisture | 0.040 | % | ||
| Processing (Melt) Temp | 255 到 270 | °C | ||
| Mold Temperature | 60 到 85 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 30.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.