Technical Data Sheet
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation?(Break) | Compression Molded | % | ASTM D-638 | 390 |
| Tensile Elongation?(Break) | Compression Molded | % | ISO 527-2 | 390 |
| Tensile Strength(Break) | Compression Molded | MPa | ASTM D-638 | 9.65 |
| Tensile Strength(Break) | Compression Molded | MPa | ISO 527-2 | 9.65 |
| Shore Hardness | Shore D | | ASTM D-2240 | |
| Shore Hardness | Shore D | | ISO 868 | |
| Tensile Modulus (2% Secant) | Compression Molded | MPa | ASTM D-638 | 33.1 |
| Tensile Modulus (2% Secant) | Compression Molded | MPa | ISO 527-2 | 33.1 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melting temperature | | ℃ | Internal Method | 77.2 |
| Vicat Softening Temperature | | ℃ | ASTM D-1525 | 42.2 |
| Vicat Softening Temperature | | ℃ | ISO 306 | 42.2 |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 125℃/2.16kg | g/10min | ASTM D-1238 | |
| Melt index | 190℃/2.16kg | g/10min | ASTM D-1238 | 300 |
| Melt index | 125℃/2.16kg | g/10min | ISO 1133 | |
| Melt index | 190℃/2.16kg | g/10min | ISO 1133 | 300 |
| monomer Content | | % | Internal Method | 20.5 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.