ASA/PC GELOY™ XP4034 SABIC INNOVATIVE NANSHA

407

Properties:
High mobility
Thermal stability
Antistatic
Weather resistance
Usages:
Automotive sector
Compare
View Prices

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	流动 : 3.20 mm	内部方法	0.50 到 0.70	%
Modeling Shrinkage	Modeling Shrinkage	横向流动 : 3.20 mm	内部方法	0.50 到 0.70	%
Moisture Absorption	24 hr	ASTM D570	0.25	%
Melt Mass-Flow Rate	220°C/10.0 kg	ASTM D1238	5.0	g/10 min
	Melt Mass-Flow Rate	260°C/5.0 kg	ASTM D1238	14	g/10 min
	Melt Mass-Flow Rate	Melt Mass-Flow Rate	280°C/3.8 kg	ASTM D1238	24	g/10 min
Outdoor Suitability		UL 746C	f2

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strain	屈服	ISO 527-2/50	4.5	%
	Tensile Strain	断裂 2	ASTM D638	25	%
	Tensile Strain	Tensile Strain	断裂	ISO 527-2/50	130	%
Tensile Modulus		ISO 527-2/1	2500	Mpa
Flexural Modulus	50.0 mm 跨距 3	ASTM D790	2510	Mpa
Flexural Modulus	Flexural Modulus	-- 4	ISO 178	2500	Mpa
Tensile Strength	屈服 2	ASTM D638	62.0	Mpa
	Tensile Strength	屈服	ISO 527-2/50	57.0	Mpa
	Tensile Strength	Tensile Strength	断裂	ISO 527-2/50	50.0	Mpa
Flexural Stress	-- 4, 5	ISO 178	75.0	Mpa
Flexural Stress	Flexural Stress	屈服, 50.0 mm 跨距 3	ASTM D790	88.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Thermal Conductivity		ASTM C177	0.25	W/m/K
Vicat Softening Temperature		ISO 306/B50	113	°C
Linear thermal expansion coefficient	流动 : -20 到 150°C	ASTM E831	7.2E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	横向 : -20 到 150°C	ASTM E831	7.2E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, 未退火, 3.20 mm	ASTM D648	115	°C
	Deflection Temperature Under Load?	0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7	ISO 75-2/Bf	116	°C
		Deflection Temperature Under Load?	1.8 MPa, 未退火, 6.40 mm	ASTM D648	104	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7	ISO 75-2/Af	98.0	°C

Injection	Test Result	Unit
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 80	%
Rear Temperature	240 到 255	°C
Middle Temperature	245 到 260	°C
Front Temperature	250 到 265	°C
Nozzle Temperature	245 到 265	°C
Back Pressure	0.300 到 1.00	Mpa
Screw Speed	30 到 80	rpm
Vent Depth	0.038 到 0.076	mm
Drying Temperature	95 到 105	°C
Suggested Max Moisture	0.040	%
Processing (Melt) Temp	260 到 275	°C
Mold Temperature	55 到 70	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	-30°C, Total Energy	ASTM D3763	30.0	J
Instrumented Dart Impact	Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	47.0	J

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R 级	ASTM D785	110

optical performance	Test Condition	Test Method	Test Result	Unit
Gardner	60°, 无织构	ASTM D523	94

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.5 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.