Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD | ASTM D955 | < 0.40 | % |
| Modeling Shrinkage | MD | ASTMD955 | <0.40 | % |
| Moisture Absorption | 饱和 | ASTMD570 | <0.30 | % |
| Moisture Absorption | 饱和 | ASTM D570 | < 0.30 | % |
| Melt Mass-Flow Rate | 200℃/5.0 kg | ASTM D1238 | 0.6 | g/10 min |
| Melt Mass-Flow Rate | 220℃/10.0 kg | ASTM D1238 | 6 | g/10 min |
| Melt Mass-Flow Rate | 200°C/5.0kg | ASTMD1238 | 0.60 | g/10min |
| Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 6.0 | g/10min |
| Density / Specific Gravity | | ASTMD792 | 1.03 | g/cm³ |
| Density / Specific Gravity | | ASTM D792 | 1.03 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Strength | 屈服,23°C | ASTMD790 | 58.6 | Mpa |
| Flexural Modulus | 23°C | ASTMD790 | 2070 | Mpa |
| Tensile Strength | 屈服,23°C,3.18mm | ASTMD638 | 38.6 | Mpa |
| Tensile Elongation | 断裂,23°C,3.18mm | ASTMD638 | 40 | % |
| Tensile Strength | Break,23°C,3.18mm | ASTMD638 | 31.7 | Mpa |
| Tensile Elongation | 断裂, 23℃, 3.18 mm | ASTM D638 | 40 | % |
| Rockwell Hardness | R 级, 23℃ | ASTM D785 | 100 | |
| Flexural Modulus | 23℃ | ASTM D790 | 2070 | Mpa |
| Flexural Strength | 屈服, 23℃ | ASTM D790 | 58.6 | Mpa |
| Tensile Strength | 屈服, 23℃, 3.18 mm | ASTM D638 | 38.6 | Mpa |
| Tensile Strength | 断裂, 23℃, 3.18 mm | ASTM D638 | 31.7 | Mpa |
| Notched Izod Impact Strength | 23℃, 3.18 mm | ASTM D256 | 360 | J/m |
| Notched Izod Impact Strength | 23℃, 6.35 mm | ASTM D256 | 310 | J/m |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ASTM D1525 | 101 | °C |
| Deflection Temperature Under Load? | 1.8 MPa, 退火, 12.7 mm | ASTM D648 | 85 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火,12.7mm | ASTMD648 | 85.0 | °C |
| Vicat Softening Temperature | | ASTMD15255 | 101 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | 23°C,3.18mm | ASTMD256 | 360 | J/m |
| Notched Izod Impact Strength | 23°C,6.35mm | ASTMD256 | 310 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R计秤,23°C | ASTMD785 | 100 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.