Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD | % | 0.80到1.0 | -- |
| Modeling Shrinkage | MD | % | 0.80到1.0 | -- |
| Melt Mass-Flow Rate | 240°C/5.0kg | g/10min | 14 | -- |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | | MPa | 45.0 | 40.0 |
| Tensile Strain | 断裂 | % | >80 | |
| Flexural Stress | | MPa | 60.0 | 50.0 |
| Flexural Modulus | 23°C | MPa | 1800 | 1600 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | -- | °C | 190 | -- |
| Vicat Softening Temperature | -- | °C | 110 | -- |
| Heat Deflection Temperature | 0.45MPa,未退火 | °C | 96.0 | -- |
| Heat Deflection Temperature | 1.8MPa,未退火 | °C | 62.0 | -- |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | 邵氏D,15秒 | | 62 | -- |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.6mm | | HB | -- |
| Glow Wire Ignition Temperature | 2.0mm | °C | 650 | -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.