PBT VALOX™ 357-1001 SABIC INNOVATIVE US

166

Properties:
Flame retardant
UV resistance
Usages:
Electrical appliances
Electronic display
Household goods
switch
Shell
Spool
Lighting fixtures
Certificates:
UL
Compare
View Prices

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD：--3	内部方法	1.2to1.6	%
	Modeling Shrinkage	MD：--2	内部方法	0.80to1.1	%
		Modeling Shrinkage	MD：--3	内部方法	1.0to1.4	%
			Modeling Shrinkage	MD：3.20mm	内部方法	1.0to1.4	%
			Modeling Shrinkage	Modeling Shrinkage	TD：--2	内部方法	0.90to1.3	%
Moisture Absorption	24hr	ASTMD570	0.080	%
	Moisture Absorption	饱和,23°C	ISO62	0.50	%
	Moisture Absorption	Moisture Absorption	平衡,23°C,50%RH	ISO62	0.15	%
Melt Mass-Flow Rate	250°C/5.0kg	ASTMD1238	9.6	g/10min
Melt Volume flow Rate	250°C/5.0kg	ISO1133	8.00	cm3/10min
Specific Volume		ASTMD792	0.740	cm³/g
Outdoor Suitability		UL746C	f2
Density / Specific Gravity		ISO1183	1.34	g/cm³
Density / Specific Gravity	Density / Specific Gravity		ASTMD792	1.35	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strain	Break	ASTMD638	54	%
Tensile Strain	Tensile Strain	Yield	ASTMD638	5.0	%
Flexural Modulus	50.0mm跨距	ASTMD790	2100	Mpa
Flexural Modulus	Flexural Modulus		ISO178	2000	Mpa
Flexural Strength		ISO178	73.0	Mpa
	Flexural Strength	屈服,50.0mm跨距	ASTMD790	78.0	Mpa
	Flexural Strength	Flexural Strength	Break,50.0mmSpan	ASTMD790	78.0	Mpa
Tensile Stress	屈服	ISO527-2/50	50.0	Mpa
Tensile Stress	Tensile Stress	断裂	ISO527-2/50	40.0	Mpa
Tensile Strain	屈服	ISO527-2/50	5.0	%
Tensile Strain	Tensile Strain	断裂	ISO527-2/50	30	%
Tensile Modulus		ISO527-2/1	2200	Mpa
Tensile Modulus	Tensile Modulus		ASTMD638	2020	Mpa
Tensile Strength	屈服	ASTMD638	48.0	Mpa
Tensile Strength	Tensile Strength	Break	ASTMD638	42.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,未退火,3.20mm	ASTMD648	135	°C
	Deflection Temperature Under Load?	0.45MPa,未退火,6.40mm	ASTMD648	138	°C
		Deflection Temperature Under Load?	1.8MPa,未退火,3.20mm	ASTMD648	98.0	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,未退火,6.40mm	ASTMD648	99.0	°C
Linear thermal expansion coefficient	MD：60to138°C	ASTME831	1.2E-04	cm/cm/°C
	Linear thermal expansion coefficient	MD：-40到40°C	ISO11359-2	7.2E-05	cm/cm/°C
		Linear thermal expansion coefficient	TD：-40到40°C	ASTME831	8.4E-05	cm/cm/°C
			Linear thermal expansion coefficient	TD：-40到40°C	ISO11359-2	8.4E-05	cm/cm/°C
			Linear thermal expansion coefficient	Linear thermal expansion coefficient	MD：-40to40°C	ASTME831	9.2E-05	cm/cm/°C
RTIElec		UL746	120	°C
Evolution Calendar intelligent importer		UL746	120	°C
RTIStr		UL746	140	°C
Heat Deflection Temperature	1.8MPa,Unannealed,64.0mmSpan	ISO75-2/Af	84.0	°C
Ball PressureTest	125°C	IEC60695-10-2	Pass
Vicat Softening Temperature		ASTMD152513	134	°C
	Vicat Softening Temperature	--	ISO306/B50	145	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B120	150	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Hot-wire Ignition	HWI	UL746	PLC2
High Amp Arc Ignition	HAI	UL746	PLC3
High Voltage Arc Tracking Rate	HVTR	UL746	PLC3
Comparative Tracking Index	CTI	UL746	PLC2
Dissipation Factor?	100Hz	ASTMD150	3E-03
Dissipation Factor?	Dissipation Factor?	1MHz	ASTMD150	0.030
Dielectric Strength	1.60mm,在油中	ASTMD149	25	KV/mm
	Dielectric Strength	3.20mm,inAir	ASTMD149	19	KV/mm
	Dielectric Strength	Dielectric Strength	3.20mm,在油中	ASTMD149	19	KV/mm
Dielectric Constant	100Hz	ASTMD150	3.20
Dielectric Constant	Dielectric Constant	1MHz	ASTMD150	3.20
Volume Resistivity		ASTMD257	>1.2E+16	ohms·cm
Arc Resistance		ASTMD495	PLC6

Impact Properties	Test Condition	Test Method	Test Result	Unit
Gardner Impact	23°C	ASTMD3029	43.4	J
Gardner Impact	Gardner Impact	23°C11	ASTMD3029	43.0	J
Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	35.8	J
Notched Izod Impact Strength	-30°C	ASTMD256	150	J/m
	Notched Izod Impact Strength	23°C	ASTMD256	320	J/m
	Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ASTMD4812	NoBreak
	23°C	ISO179/1eA	45	kJ/m²
Notched Izod Impact Strength	-30°C	ISO180/1A	10	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	45	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R级	ASTMD785	117

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.46mm	UL94	HB
	UL flame retardant rating	0.63mm	UL94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	5VA
Glow Wire Flammability Index	1.0mm	IEC60695-2-12	960	°C
Glow Wire Ignition Temperature	1.0mm	IEC60695-2-13	775	°C
	Glow Wire Ignition Temperature	2.0mm	IEC60695-2-13	750	°C
	Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0mm	IEC60695-2-13	725	°C
Oxygen Index		ASTMD2863	30	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

PBT VALOX™ 357-1001 SABIC INNOVATIVE US

Technical Data Sheet